颗粒：
、
、物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 | ||
| Tensile Modulus | 7.90 GPa | 1150 ksi | ISO 527 | ||
| Flexural Modulus | 7.96 GPa | 1150 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 4.40 kJ/m² @Temperature -40.0 °C |
2.09 ft-lb/in² @Temperature -40.0 °F |
ISO 180 | ||
| 5.20 kJ/m² @Temperature 23.0 °C |
2.47 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |||
| Charpy Impact, Notched | 0.440 J/cm² | 2.09 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ISO 3146 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | |||
| Mold Temperature | 80.0 - 95.0 °C | 176 - 203 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.10 % | <= 0.10 % | |||
| Injection Pressure | 35.0 - 125 MPa | 5080 - 18100 psi | |||
| De |
|||||
| Color | BK 23210 | ||||
| Commercial Status | North America | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。