颗粒样图：
、
、应用：广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com
物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | dry; ISO 1183 |
| Water Absorption | 4.5 % | 4.5 % | Sim. To ISO 62 |
| Moisture Absorption | 1.30 % | 1.30 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0021 cm/cm | 0.0021 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0077 cm/cm | 0.0077 in/in | Sim. To ISO 294 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 100 MPa | 14500 psi | cond; ISO 527-1/-2 |
| 150 MPa | 21800 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 2.5 % | 2.5 % | dry; ISO 527-1/-2 |
| 5.0 % | 5.0 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 7.03 GPa | 1020 ksi | cond; ISO 527-1/-2 |
| 11.5 GPa | 1670 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 5.98 J/cm² @Temperature 23.0 °C |
28.5 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU |
| 5.98 J/cm² @Temperature -30.0 °C |
28.5 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eU | |
| 5.98 J/cm² @Temperature 23.0 °C |
28.5 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| 5.98 J/cm² @Temperature -30.0 °C |
28.5 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA |
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA | |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | cond; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | cond; IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| 3.5 @Frequency 100 Hz |
3.5 @Frequency 100 Hz |
dry; IEC 60250 | |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
cond; IEC 60250 | |
| 10 @Frequency 100 Hz |
10 @Frequency 100 Hz |
cond; IEC 60250 | |
| Dissipation Factor | 0.0060 @Frequency 100 Hz |
0.0060 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.012 @Frequency 1.00e+6 Hz |
0.012 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| 0.070 @Frequency 1.00e+6 Hz |
0.070 @Frequency 1.00e+6 Hz |
cond; IEC 60250 | |
| 0.30 @Frequency 100 Hz |
0.30 @Frequency 100 Hz |
cond; IEC 60250 | |
| Comparative Tracking Index | 325 V | 325 V | dry; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
dry; IEC 60695-11-10 |
| V-0 @Thickness 0.749 mm |
V-0 @Thickness 0.0295 in |
dry; IEC 60695-11-10 |
|