PA6 1015G35NAT 性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

颗粒：

、

物性表:

Physical Properties	Metric	English	Comments

Density	1.41 g/cc	0.0509 lb/in³	dry; ISO 1183
Moisture Absorption	2.30 %	2.30 %	Sim. To ISO 62
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	120 MPa	17400 psi	cond; ISO 527-1/-2
	190 MPa	27600 psi	dry; ISO 527-1/-2
Elongation at Break	2.6 %	2.6 %	dry; ISO 527-1/-2
	6.0 %	6.0 %	cond; ISO 527-1/-2
Tensile Modulus	6.30 GPa	914 ksi	cond; ISO 527-1/-2
	11.4 GPa	1650 ksi	dry; ISO 527-1/-2
Flexural Strength	195 MPa	28300 psi	cond; ISO 178
	295 MPa	42800 psi	dry; ISO 178
Flexural Modulus	6.60 GPa	957 ksi	cond; ISO 178
	9.80 GPa	1420 ksi	dry; ISO 178
Charpy Impact Unnotched	9.60 J/cm² @Temperature 23.0 °C	45.7 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eU
	10.8 J/cm² @Temperature 23.0 °C	51.4 ft-lb/in² @Temperature 73.4 °F	cond; ISO 179/1eU
Charpy Impact, Notched	1.40 J/cm² @Temperature 23.0 °C	6.66 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eA
	2.40 J/cm² @Temperature 23.0 °C	11.4 ft-lb/in² @Temperature 73.4 °F	cond; ISO 179/1eA

Electrical Properties	Metric	English	Comments
Volume Resistivity	7.00e+14 ohm-cm	7.00e+14 ohm-cm	dry; IEC 60093
Surface Resistance	3.00e+13 ohm	3.00e+13 ohm	cond; IEC 60093
Dielectric Constant	4.0 @Frequency 100 Hz	4.0 @Frequency 100 Hz	dry; IEC 60250
	4.0 @Frequency 1.00e+6 Hz	4.0 @Frequency 1.00e+6 Hz	dry; IEC 60250
Dielectric Strength	23.0 kV/mm	584 kV/in	dry; IEC 60243-1
Dissipation Factor	0.011 @Frequency 100 Hz	0.011 @Frequency 100 Hz	dry; IEC 60250
	0.019 @Frequency 1.00e+6 Hz	0.019 @Frequency 1.00e+6 Hz	dry; IEC 60250
Comparative Tracking Index	400 V	400 V	dry; IEC 60112

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	220 °C	428 °F	dry; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	206 °C	403 °F	dry; ISO 75-1/-2
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	dry; IEC 60695-11-10

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。