| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.90 % | 1.90 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 150 MPa | 21800 psi | cond; ISO 527-1/-2 |
| 220 MPa | 31900 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 |
| 6.0 % | 6.0 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 8.00 GPa | 1160 ksi | cond; ISO 527-1/-2 |
| 13.6 GPa | 1970 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 230 MPa | 33400 psi | cond; ISO 178 |
| 355 MPa | 51500 psi | dry; ISO 178 | |
| Flexural Modulus | 8.80 GPa | 1280 ksi | cond; ISO 178 |
| 13.6 GPa | 1970 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 11.0 J/cm² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 13.0 J/cm² @Temperature 23.0 °C |
61.9 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 2.70 J/cm² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | dry; IEC 60093 |
| Surface Resistance | 3.00e+13 ohm | 3.00e+13 ohm | cond; IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| 5.0 @Frequency 100 Hz |
5.0 @Frequency 100 Hz |
dry; IEC 60250 | |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | dry; IEC 60243-1 |
| Dissipation Factor | 0.024 @Frequency 1.00e+6 Hz |
0.024 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| 0.028 @Frequency 100 Hz |
0.028 @Frequency 100 Hz |
dry; IEC 60250 | |
| Comparative Tracking Index | 400 V | 400 V | dry; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 209 °C | 408 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
dry; IEC 60695-11-10 |
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。