颗粒：
、
、物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | |||
| Linear Mold Shrinkage, Flow | 0.00350 - 0.00500 cm/cm | 0.00350 - 0.00500 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.00800 - 0.0110 cm/cm | 0.00800 - 0.0110 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 27.0 MPa @Temperature 150 °C |
3920 psi @Temperature 302 °F |
|||
| 40.0 MPa @Temperature 120 °C |
5800 psi @Temperature 248 °F |
||||
| 53.0 MPa @Temperature 90.0 °C |
7690 psi @Temperature 194 °F |
||||
| 78.0 MPa @Temperature 60.0 °C |
11300 psi @Temperature 140 °F |
||||
| 125 MPa @Temperature 23.0 °C |
18100 psi @Temperature 73.4 °F |
||||
| Elongation at Break | 2.70 % @Temperature 23.0 °C |
2.70 % @Temperature 73.4 °F |
|||
| 4.60 % @Temperature 60.0 °C |
4.60 % @Temperature 140 °F |
||||
| 6.00 % @Temperature 90.0 °C |
6.00 % @Temperature 194 °F |
||||
| 6.70 % @Temperature 120 °C |
6.70 % @Temperature 248 °F |
||||
| 7.50 % @Temperature 150 °C |
7.50 % @Temperature 302 °F |
||||
| Elongation at Yield | 4.00 % @Temperature 60.0 °C |
4.00 % @Temperature 140 °F |
|||
| 5.00 % @Temperature 90.0 °C |
5.00 % @Temperature 194 °F |
||||
| 6.00 % @Temperature 120 °C |
6.00 % @Temperature 248 °F |
||||
| 6.80 % @Temperature 150 °C |
6.80 % @Temperature 302 °F |
||||
| Tensile Modulus | 2.10 GPa @Temperature 150 °C |
305 ksi @Temperature 302 °F |
|||
| 3.10 GPa @Temperature 120 °C |
450 ksi @Temperature 248 °F |
||||
| 4.70 GPa @Temperature 90.0 °C |
682 ksi @Temperature 194 °F |
||||
| 6.40 GPa @Temperature 60.0 °C |
928 ksi @Temperature 140 °F |
||||
| 9.40 GPa @Temperature 23.0 °C |
1360 ksi @Temperature 73.4 °F |
||||
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
|||
| 5.50 J/cm² @Temperature -20.0 °C |
26.2 ft-lb/in² @Temperature -4.00 °F |
||||
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -20.0 °C |
3.81 ft-lb/in² @Temperature -4.00 °F |
|||
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 120 °C | 248 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | |||
| Vicat Softening Point | 170 °C @Load 5.00 kg |
338 °F @Load 11.0 lb |
|||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | |||
| Mold Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
|||
| De |
|||||
| ISO Shrinkage - Pressure | 60 MPa | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。