PA6 HI5063A PA6/ABS+MF6%, 高冲击、_产品资讯

PA6 HI5063A 聚酰胺俗称尼龙（Nylon），英文名称Polyamide（简称PA），是分子主链上含有重复酰胺基团—[NHCO]—的热塑性树脂总称。包括脂肪族PA，脂肪—芳香族PA和芳香族PA。其中，脂肪族PA品种多，产量大，应用广泛，其命名由合成单体具体的碳原子数而定。

颗粒图：

、

用途：

广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。

电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座。

汽车：散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座。

工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输。

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。

PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。

欢迎各位客户前来咨询：

联系人：夏先生

手机：13501802636

QQ ：205730283

邮箱：205730283@qq.com

物性表:

Physical Properties	Metric	English	Comments

Specific Gravity	1.09 g/cc	1.09 g/cc	ASTM D792
Water Absorption	0.60 %	0.60 %	ASTM D570
Linear Mold Shrinkage, Flow	0.0050 - 0.010 cm/cm @Thickness 3.20 mm	0.0050 - 0.010 in/in @Thickness 0.126 in	ASTM D955
Melt Flow	8.0 g/10 min	8.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	47.0 MPa @Thickness 3.20 mm	6810 psi @Thickness 0.126 in	50mm/min; ASTM D638
Elongation at Break	50 % @Thickness 3.20 mm	50 % @Thickness 0.126 in	50mm/min; ASTM D638
Flexural Yield Strength	67.0 MPa @Thickness 6.40 mm	9710 psi @Thickness 0.252 in	2.8mm/min; ASTM D790
Flexural Modulus	2.2599 GPa @Thickness 6.40 mm	327.78 ksi @Thickness 0.252 in	2.8mm/min; ASTM D790
Izod Impact, Notched	1.90 J/cm @Thickness 3.20 mm, Temperature 23.0 °C	3.56 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	65.0 - 100 µm/m-°C	36.1 - 55.6 µin/in-°F	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	90.0 °C @Thickness 6.40 mm	194 °F @Thickness 0.252 in	Unannealed; ASTM D648
UL RTI, Electrical	60.0 °C @Thickness >=0.750 mm	140 °F @Thickness >=0.0295 in
	60.0 °C @Thickness >=1.50 mm	140 °F @Thickness >=0.0591 in
	60.0 °C @Thickness >=3.00 mm	140 °F @Thickness >=0.118 in
UL RTI, Mechanical with Impact	60.0 °C @Thickness >=0.750 mm	140 °F @Thickness >=0.0295 in
	60.0 °C @Thickness >=1.50 mm	140 °F @Thickness >=0.0591 in
	60.0 °C @Thickness >=3.00 mm	140 °F @Thickness >=0.118 in
UL RTI, Mechanical without Impact	60.0 °C @Thickness >=0.750 mm	140 °F @Thickness >=0.0295 in
	60.0 °C @Thickness >=1.50 mm	140 °F @Thickness >=0.0591 in
	60.0 °C @Thickness >=3.00 mm	140 °F @Thickness >=0.118 in
Flammability, UL94	HB @Thickness >=0.800 mm	HB @Thickness >=0.0315 in
	HB @Thickness >=1.60 mm	HB @Thickness >=0.0630 in
	HB @Thickness >=2.50 mm	HB @Thickness >=0.0984 in
	HB @Thickness >=3.20 mm	HB @Thickness >=0.126 in

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	245 - 260 °C	473 - 500 °F	Injection Molding
Middle Barrel Temperature	250 - 270 °C	482 - 518 °F	Injection Molding
Front Barrel Temperature	260 - 270 °C	500 - 518 °F	Injection Molding
Nozzle Temperature	260 - 275 °C	500 - 527 °F	Injection Molding
Melt Temperature	260 - 275 °C	500 - 527 °F	Injection Molding
Mold Temperature	80.0 - 100 °C	176 - 212 °F	Injection Molding
Drying Temperature	70.0 - 90.0 °C	158 - 194 °F	Injection Molding
Dry Time	4.00 - 5.00 hour	4.00 - 5.00 hour	Injection Molding