原料颗粒图：
、
、物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183-1 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | ISO 2039-1 |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 100 MPa | 14500 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-1,-2 |
| 3.0 % | 3.0 % | Nominal, 5 mm/min; ISO 527-1,-2 | |
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 6.50 GPa | 943 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.10 GPa | 885 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 180-A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 180-A | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ISO 75-1,-2 |
| Vicat Softening Point | 140 °C @Load 5.10 kg |
284 °F @Load 11.2 lb |
120°C/h; ISO 306 |
| Shrinkage | <= 0.10 % | <= 0.10 % | post-shrinkage; b.o. ISO 2577 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 °C | 500 °F | Injection molding; ISO 294 |
| Mold Temperature | 70.0 °C | 158 °F | Injection molding; ISO 294 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |