PBT/T835FRUV NC010/ PBT、

 PBT/T835FRUV NC010/ 是最坚韧的工程热塑材料之一，PBT/T835FRUV NC010/ 它是半结晶材料，PBT/T835FRUV NC010/ 有非常好的化学稳定性、机械强度、电绝缘特性和热稳定性。这些材料在很广的环境条件下都有很好的稳定性。PBT吸湿特性很弱。非增强型PBT的张力强度为50MPa，玻璃添加剂型的PBT张力强度为170MPa。玻璃添加剂过多将导致材料变脆。

Physical Properties	Metric	English	Comments
Density	1.43 g/cc	0.0517 lb/in³	ISO 1183
Filler Content	5.0 %	5.0 %
Linear Mold Shrinkage	0.013 cm/cm @Thickness 3.20 mm	0.013 in/in @Thickness 0.126 in	Transverse
	0.014 cm/cm @Thickness 3.20 mm	0.014 in/in @Thickness 0.126 in	Flow
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.0 MPa @Temperature 23.0 °C	8700 psi @Temperature 73.4 °F	ASTM D638
	62.0 MPa @Temperature 23.0 °C	8990 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	5.0 % @Temperature 23.0 °C	5.0 % @Temperature 73.4 °F	ISO 527
	5.0 % @Temperature 23.0 °C	5.0 % @Temperature 73.4 °F	ASTM D638
Tensile Modulus	3.40 GPa @Temperature 23.0 °C	493 ksi @Temperature 73.4 °F	ISO 527
Flexural Modulus	3.10 GPa @Temperature 23.0 °C	450 ksi @Temperature 73.4 °F	ISO 178
	3.20 GPa @Temperature 23.0 °C	464 ksi @Temperature 73.4 °F	ASTM D790
Izod Impact, Notched	1.50 J/cm @Temperature 23.0 °C	2.81 ft-lb/in @Temperature 73.4 °F	ASTM D256
Izod Impact, Notched (ISO)	9.00 kJ/m² @Temperature 23.0 °C	4.28 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Izod Impact, Unnotched (ISO)	45.0 kJ/m² @Temperature 23.0 °C	21.4 ft-lb/in² @Temperature 73.4 °F	ISO 180/1U
Charpy Impact Unnotched	5.50 J/cm² @Temperature 23.0 °C	26.2 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.900 J/cm² @Temperature 23.0 °C	4.28 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA
Thermal Properties	Metric	English	Comments
Melting Point	223 °C	433 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	120 °C	248 °F	ISO 75-1/-2
UL RTI, Electrical	130 °C @Thickness 0.800 mm	266 °F @Thickness 0.0315 in	UL 746B
	130 °C @Thickness 1.50 mm	266 °F @Thickness 0.0591 in	UL 746B
	130 °C @Thickness 3.00 mm	266 °F @Thickness 0.118 in	UL 746B
UL RTI, Mechanical with Impact	130 °C @Thickness 0.800 mm	266 °F @Thickness 0.0315 in	UL 746B
	130 °C @Thickness 1.50 mm	266 °F @Thickness 0.0591 in	UL 746B
	130 °C @Thickness 3.00 mm	266 °F @Thickness 0.118 in	UL 746B
UL RTI, Mechanical without Impact	130 °C @Thickness 0.800 mm	266 °F @Thickness 0.0315 in	UL 746B
	130 °C @Thickness 1.50 mm	266 °F @Thickness 0.0591 in	UL 746B
	130 °C @Thickness 3.00 mm	266 °F @Thickness 0.118 in	UL 746B
Flammability, UL94	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in	UL94
	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	UL94
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	UL94
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	IEC 60695-11-10
	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	IEC 60695-11-10
	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in	IEC 60695-11-10
Processing Properties	Metric	English	Comments
Melt Temperature	240 - 260 °C	464 - 500 °F
	250 °C	482 °F	Optimum
Mold Temperature	80.0 °C	176 °F	optimum
	30.0 - 130 °C	86.0 - 266 °F
Drying Temperature	110 - 130 °C	230 - 266 °F
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour
Moisture Content	<= 0.040 %	<= 0.040 %
Descriptive Properties
Appearance	Natural Color
Drying Recommended	Yes
Filler	Glass fiber reinforcement
Generic	PBT
Material Status	Current
Part Marking Code	>PBT-IGF5FR(17)<	ISO 11469
Polymer Family	Polyester
Polymer Type	PBT
Product Category	Flame Retardant Resins
	Glass Reinforced Resins
	Toughened Resins
	UV Resistant/Weatherable Resins
Resin Identification	PBT-IGF5FR(17)	ISO 1043
RoHS Compliance	Contact Manufacturer