类别：聚合物；热塑性塑料；聚碳酸酯（聚碳酸酯）
材料说明：
发展产物
注塑级
9%矿物填充
耐热性很高
线性热膨胀系数降低
拉伸模量= 3350兆帕
维卡/ B 120 = 142°C
预处理
最大水含量0.01-0.05%
干燥温度100-110°C
干燥时间
空气清新机（高速机）h
干空气干燥2-4小时
必须小心，以确保颗粒在一个充分干燥的状态下进行处理。
处理
熔体温度240-280°C
模具温度70-100°C
物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.60 % | 0.60 % | Similar to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | Similar to ISO 62 | ||
| Melt Flow | 22 g/10 min @Load 5.00 kg, Temperature 260 °C |
22 g/10 min @Load 11.0 lb, Temperature 500 °F |
estimated from MVR using room temperature density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | ISO 527-1/-2 | ||
| Elongation at Yield | 4.6 % | 4.6 % | ISO 527-1/-2 | ||
| Tensile Modulus | 3.35 GPa | 486 ksi | ISO 527-1/-2 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.2 @Frequency 100 Hz |
3.2 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0015 @Frequency 100 Hz |
0.0015 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 55.0 µm/m-°C | 30.6 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 65.0 µm/m-°C | 36.1 µin/in-°F | ISO 11359-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C | 277 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 140 °C | 284 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 0.900 mm |
HB @Thickness 0.0354 in |
IEC 60695-11-10 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |||
| 260 °C | 500 °F | Injection Molding; ISO 294 | |||
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 | ||
| 70.0 - 100 °C | 158 - 212 °F | ||||
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 | ||
| De |
|||||
| Availability | Asia Pacific | ||||
| Europe | |||||
| Near East/Africa | |||||
| South and Central America | |||||
| Feature | Heat stabilised or stable to heat | ||||
| Release agent | |||||
| Form | Pellets | ||||
| Process | Injection Molding | ||||
| UL recognition | UL\lh\n | ||||