| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.650 - 0.900 g/cc | 0.0235 - 0.0325 lb/in³ | |||
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.80 % | 0.80 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.021 cm/cm | 0.021 in/in | ISO 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.021 cm/cm | 0.021 in/in | ISO 2577 | ||
| Melt Flow | 10.65 g/10 min @Load 2.16 kg, Temperature 190 °C |
10.65 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 140 MPa @Load 36.5 kg, Time 30.0 sec |
20300 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 | ||
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Break | 26 % | 26 % | ISO 527-2 | ||
| Elongation at Yield | 8.5 % | 8.5 % | ISO 527-2 | ||
| Modulus of Elasticity | 2.80 GPa | 406 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 15.0 J/cm² @Temperature -30.0 °C |
71.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| 15.0 J/cm² @Temperature 23.0 °C |
71.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.350 J/cm² @Temperature -30.0 °C |
1.67 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
| 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1000 hours | 1400 MPa @Strain <=0.500 % |
203000 psi @Strain <=0.500 % |
ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0010 @Frequency 100 Hz |
0.0010 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0050 @Frequency 1.00e+6 Hz |
0.0050 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| 600 V | 600 V | Test solution B; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
DIN 53752 | ||
| Melting Point | 166 °C | 331 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 100 °C | 212 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75-2 | ||
| Vicat Softening Point | 150 °C | 302 °F | ISO 306 | ||
| Decomposition Temperature | >= 240 °C | >= 464 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 200 °C | 392 °F | Hopper Throat | ||
| Zone 1 | 200 °C | 392 °F | Feed zone | ||
| Zone 2 | 200 °C | 392 °F | Compression | ||
| Zone 3 | 200 °C | 392 °F | Metering-zone | ||
| Zone 4 | 200 °C | 392 °F | Nozzle | ||
| Melt Temperature | 200 °C | 392 °F | Optimal | ||
| 190 - 230 °C | 374 - 446 °F | Injection-molding | |||
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | Injection-molding | ||
| 90.0 °C | 194 °F | Optimal | |||
| Drying Temperature | 100 °C | 212 °F | |||
| Dry Time | 3 hour | 3 hour | |||
| De |
|||||
| Commercial Status | Europe | ||||
| Ignition Temperature | 320 - 340°C | ASTM D1929 | |||
| Peripheral Screw Speed | <0.3 m/s | ||||
| Primary Processing Technique | Injection Molding | ||||
POM 的简介
聚甲醛是一种表面光滑，有光泽的硬而致密的材料，淡黄或白色，可在-40- 100°C温度范围内长期使用。它的耐磨性和自润滑性也比绝大多数工程塑料优越，又有良好的耐油，耐过氧化物性能。很不耐酸，不耐强碱和不耐紫外线的辐射。
POM 物理性质
聚甲醛的拉伸强度达70MPa，吸水性小，尺寸稳定，有光泽，这些性能都比尼龙好，聚甲醛为高度结晶的树脂，在热塑性树脂中是最坚韧的。具抗热强度，弯曲强度，耐疲劳性强度均高，耐磨性和电性能优良。
POM 聚甲醛的性能:
性 能 数 值
比重 1.43
熔点 175°C
伸强度（屈服） 70MPa
伸长率（屈服） 15%
（断裂） 15%
冲击强度（无缺口） 108KJ/m2
（带缺口） 7.6KJ/m2
应用范围
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。