| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.021 cm/cm | 0.021 in/in | ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ISO 294-4 2577 | ||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
cm³/10min; ISO 1133 | ||
| 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 18.4 MPa @Strain 0.700 %, Temperature 23.0 °C |
2670 psi @Strain 0.700 %, Temperature 73.4 °F |
ISO 11403-1 -2 | ||
| 49.0 MPa @Strain 1.50 %, Temperature -40.0 °C |
7110 psi @Strain 1.50 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 54.9 MPa @Strain 3.10 %, Temperature 23.0 °C |
7960 psi @Strain 3.10 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 62.8 MPa @Strain 5.00 %, Temperature 23.0 °C |
9110 psi @Strain 5.00 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 66.7 MPa @Strain 8.00 %, Temperature 23.0 °C |
9670 psi @Strain 8.00 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 91.0 MPa @Strain 6.00 %, Temperature -40.0 °C |
13200 psi @Strain 6.00 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 95.4 MPa @Strain 12.0 %, Temperature -40.0 °C |
13800 psi @Strain 12.0 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| Tensile Strength, Yield | 71.0 MPa | 10300 psi | ISO 527-1/-2 | ||
| Elongation at Break | 40 % | 40 % | Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 22 % | 22 % | ISO 527-1/-2 | ||
| Tensile Modulus | 3.05 GPa | 442 ksi | ISO 527-1/-2 | ||
| Secant Modulus | 0.482857 GPa @Strain 14.0 %, Temperature 23.0 °C |
70.0336 ksi @Strain 14.0 %, Temperature 73.4 °F |
ISO 11403-1 -2 | ||
| 0.520 GPa @Strain 7.00 %, Temperature 80.0 °C |
75.4 ksi @Strain 7.00 %, Temperature 176 °F |
ISO 11403-1 -2 | |||
| 0.524 GPa @Strain 5.00 %, Temperature 100 °C |
76.0 ksi @Strain 5.00 %, Temperature 212 °F |
ISO 11403-1 -2 | |||
| 0.530556 GPa @Strain 18.0 %, Temperature -40.0 °C |
76.9518 ksi @Strain 18.0 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 0.660606 GPa @Strain 3.30 %, Temperature 100 °C |
95.8143 ksi @Strain 3.30 %, Temperature 212 °F |
ISO 11403-1 -2 | |||
| 0.77619 GPa @Strain 4.20 %, Temperature 80.0 °C |
112.58 ksi @Strain 4.20 %, Temperature 176 °F |
ISO 11403-1 -2 | |||
| 0.8625 GPa @Strain 1.60 %, Temperature 100 °C |
125.1 ksi @Strain 1.60 %, Temperature 212 °F |
ISO 11403-1 -2 | |||
| 0.950 GPa @Strain 0.400 %, Temperature 100 °C |
138 ksi @Strain 0.400 %, Temperature 212 °F |
ISO 11403-1 -2 | |||
| 1.07 GPa @Strain 6.00 %, Temperature 23.0 °C |
155 ksi @Strain 6.00 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 1.07619 GPa @Strain 2.10 %, Temperature 80.0 °C |
156.091 ksi @Strain 2.10 %, Temperature 176 °F |
ISO 11403-1 -2 | |||
| 1.46 GPa @Strain 0.500 %, Temperature 80.0 °C |
212 ksi @Strain 0.500 %, Temperature 176 °F |
ISO 11403-1 -2 | |||
| 1.51667 GPa @Strain 6.00 %, Temperature -40.0 °C |
219.978 ksi @Strain 6.00 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 1.77097 GPa @Strain 3.10 %, Temperature 23.0 °C |
256.861 ksi @Strain 3.10 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 2.62857 GPa @Strain 0.700 %, Temperature 23.0 °C |
381.248 ksi @Strain 0.700 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 3.26667 GPa @Strain 1.50 %, Temperature -40.0 °C |
473.798 ksi @Strain 1.50 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| 31.0 J/cm² @Temperature -30.0 °C |
148 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA | ||
| 0.950 J/cm² @Temperature -30.0 °C |
4.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-1/-2 | ||
| De |
|||||
| Additives | Release agent | ||||
| Delivery form | Pellets | ||||
| Part Marking Code | >POM< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | POM | ISO 1043 |
|||
POM 的简介
POM强度、刚度高，弹性好，减磨耐磨性好。其力学性能优异，比强度可达50.5MPa，比刚度可达2650MPa，与金属十分接近。POM的力学性能随温度变化小，共聚POM比均聚POM的变化稍大一点。
POM的冲击强度较高，但常规冲击不及ABS和PC；POM对缺口敏感，有缺口可使冲击强度下降90%之多。
POM的疲劳强度十分突出，10交变载荷作用后，疲劳强度可达35MPa，而PA和PC仅为28MPa。
POM的蠕变性与PA相似，在20℃、21MPa、3000h时仅为2.3%，而且受温度的影响很小。
POM的摩擦因数小，耐磨性好（POM>PA66>PA6>ABS>HPVC>PS>PC），极限PV值很大，自润滑性好。
POM制品对磨时，高载荷作用时易产生类似尖叫的噪声。
POM 化学性质
POM 按分子链结构不同，聚甲醛可分为均聚甲醛和共聚甲醛，前者密度、结晶度、熔点都高，但是热稳定性差，加工温度窄（10度），对酸堿的稳定性略低；后者密度、结晶度、熔点较低，但热稳定性好，不易分解，加工温度宽（50度） 。
POM 不足之处在于：由受强酸腐蚀，耐侯差，粘合性差，热分解与软化温度接近，限氧指数小。它们广泛用于汽车工业，电子电器，机械设备等。还可以做水龙头、框窗、洗漱盆。
POM具有很低的摩擦系数和很好的几何稳定性，特别适合于制作齿轮和轴承。由于它还具有耐高温特性，因此还用于管道器件（管道阀门、泵壳体），草坪设备等。
POM 环境性能:
POM不耐强酸和氧化剂，对烯酸及弱酸有一定的稳定性。
POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。
POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。
应用范围
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。