  4. POM 311DP NC010,杜邦,易于加工 增强部分性能

POM 311DP NC010,杜邦,易于加工 增强部分性能

杜邦高性能聚合物聚甲醛（POM）®311DP NC010乙缩醛 类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋 材料说明：核中高粘度缩醛均聚物 Delrin 311DP是中高粘度缩醛均聚物具有增强的结晶和部分性能和易于加工的平衡。它具有改善高强度和高强度
POM 311DP NC010 的物性表：
 
Physical Properties Metric English Comments
Density  1.42 g/cc 0.0513 lb/in³ ISO 1183
Water Absorption  0.90 %
@Thickness 2.00 mm		 0.90 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.200 %
@Thickness 2.00 mm		 0.200 %
@Thickness 0.0787 in		 Sim. to ISO 62
Linear Mold Shrinkage, Flow  0.019 cm/cm 0.019 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.018 cm/cm 0.018 in/in ISO 294-4 2577
Melt Flow   6.0 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 6.0 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 cm³/10min; ISO 1133
  7.0 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 7.0 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Stress   4.47 MPa
@Strain 0.150 %,
Temperature 40.0 °C		 648 psi
@Strain 0.150 %,
Temperature 104 °F		 ISO 11403-1 -2
  6.31 MPa
@Strain 0.460 %,
Temperature 90.0 °C		 915 psi
@Strain 0.460 %,
Temperature 194 °F		 ISO 11403-1 -2
  9.92 MPa
@Strain 0.290 %,
Temperature 23.0 °C		 1440 psi
@Strain 0.290 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  21.3 MPa
@Strain 0.611 %,
Temperature 0.000 °C		 3090 psi
@Strain 0.611 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  24.56 MPa
@Strain 2.58 %,
Temperature 90.0 °C		 3562 psi
@Strain 2.58 %,
Temperature 194 °F		 ISO 11403-1 -2
  27.19 MPa
@Strain 0.730 %,
Temperature -20.0 °C		 3944 psi
@Strain 0.730 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  27.45 MPa
@Strain 0.690 %,
Temperature -40.0 °C		 3981 psi
@Strain 0.690 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  32.21 MPa
@Strain 4.88 %,
Temperature 90.0 °C		 4672 psi
@Strain 4.88 %,
Temperature 194 °F		 ISO 11403-1 -2
  37.04 MPa
@Strain 1.71 %,
Temperature 40.0 °C		 5372 psi
@Strain 1.71 %,
Temperature 104 °F		 ISO 11403-1 -2
  50.17 MPa
@Strain 2.29 %,
Temperature 23.0 °C		 7277 psi
@Strain 2.29 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  54.39 MPa
@Strain 3.93 %,
Temperature 40.0 °C		 7889 psi
@Strain 3.93 %,
Temperature 104 °F		 ISO 11403-1 -2
  56.48 MPa
@Strain 2.29 %,
Temperature 0.000 °C		 8192 psi
@Strain 2.29 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  60.28 MPa
@Strain 6.41 %,
Temperature 40.0 °C		 8743 psi
@Strain 6.41 %,
Temperature 104 °F		 ISO 11403-1 -2
  64.31 MPa
@Strain 4.58 %,
Temperature 23.0 °C		 9327 psi
@Strain 4.58 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  68.72 MPa
@Strain 7.21 %,
Temperature 23.0 °C		 9967 psi
@Strain 7.21 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  72.85 MPa
@Strain 4.53 %,
Temperature 0.000 °C		 10570 psi
@Strain 4.53 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  75.19 MPa
@Strain 3.25 %,
Temperature -20.0 °C		 10910 psi
@Strain 3.25 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  77.78 MPa
@Strain 7.12 %,
Temperature 0.000 °C		 11280 psi
@Strain 7.12 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  80.68 MPa
@Strain 3.12 %,
Temperature -40.0 °C		 11700 psi
@Strain 3.12 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  85.65 MPa
@Strain 5.67 %,
Temperature -20.0 °C		 12420 psi
@Strain 5.67 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  88.5 MPa
@Strain 8.47 %,
Temperature -20.0 °C		 12800 psi
@Strain 8.47 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  93.8 MPa
@Strain 5.11 %,
Temperature -40.0 °C		 13600 psi
@Strain 5.11 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  97.6 MPa
@Strain 7.38 %,
Temperature -40.0 °C		 14200 psi
@Strain 7.38 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Tensile Strength, Yield  74.0 MPa 10700 psi ISO 527-1/-2
Elongation at Break  35 % 35 % Nominal; ISO 527-1/-2
Elongation at Yield  15 % 15 % ISO 527-1/-2
Tensile Modulus  3.30 GPa 479 ksi ISO 527-1/-2
Flexural Strength  86.0 MPa
@Strain 3.50 %		 12500 psi
@Strain 3.50 %		 ISO 178
Flexural Modulus  3.10 GPa 450 ksi ISO 178
Secant Modulus   0.570 GPa
@Strain 5.00 %,
Temperature 100 °C		 82.7 ksi
@Strain 5.00 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.591429 GPa
@Strain 7.00 %,
Temperature 80.0 °C		 85.7809 ksi
@Strain 7.00 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.736364 GPa
@Strain 3.30 %,
Temperature 100 °C		 106.802 ksi
@Strain 3.30 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.754156 GPa
@Strain 8.18 %,
Temperature 40.0 °C		 109.383 ksi
@Strain 8.18 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.9075 GPa
@Strain 4.00 %,
Temperature 80.0 °C		 131.6 ksi
@Strain 4.00 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.99375 GPa
@Strain 1.60 %,
Temperature 100 °C		 144.13 ksi
@Strain 1.60 %,
Temperature 212 °F		 ISO 11403-1 -2
  1.15 GPa
@Strain 0.400 %,
Temperature 100 °C		 167 ksi
@Strain 0.400 %,
Temperature 212 °F		 ISO 11403-1 -2
  1.2163 GPa
@Strain 5.46 %,
Temperature 23.0 °C		 176.41 ksi
@Strain 5.46 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  1.21638 GPa
@Strain 4.70 %,
Temperature 40.0 °C		 176.424 ksi
@Strain 4.70 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.255 GPa
@Strain 2.00 %,
Temperature 80.0 °C		 182.0 ksi
@Strain 2.00 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.32683 GPa
@Strain 6.56 %,
Temperature -20.0 °C		 192.443 ksi
@Strain 6.56 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  1.39777 GPa
@Strain 5.38 %,
Temperature 0.000 °C		 202.733 ksi
@Strain 5.38 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  1.63106 GPa
@Strain 5.86 %,
Temperature -40.0 °C		 236.569 ksi
@Strain 5.86 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  1.64 GPa
@Strain 0.500 %,
Temperature 80.0 °C		 238 ksi
@Strain 0.500 %,
Temperature 176 °F		 ISO 11403-1 -2
  2.16608 GPa
@Strain 1.71 %,
Temperature 40.0 °C		 314.168 ksi
@Strain 1.71 %,
Temperature 104 °F		 ISO 11403-1 -2
  2.19083 GPa
@Strain 2.29 %,
Temperature 23.0 °C		 317.758 ksi
@Strain 2.29 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.31354 GPa
@Strain 3.25 %,
Temperature -20.0 °C		 335.556 ksi
@Strain 3.25 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  2.46638 GPa
@Strain 2.29 %,
Temperature 0.000 °C		 357.724 ksi
@Strain 2.29 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.5859 GPa
@Strain 3.12 %,
Temperature -40.0 °C		 375.06 ksi
@Strain 3.12 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.98 GPa
@Strain 0.150 %,
Temperature 40.0 °C		 432 ksi
@Strain 0.150 %,
Temperature 104 °F		 ISO 11403-1 -2
  3.42069 GPa
@Strain 0.290 %,
Temperature 23.0 °C		 496.137 ksi
@Strain 0.290 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  3.48609 GPa
@Strain 0.611 %,
Temperature 0.000 °C		 505.622 ksi
@Strain 0.611 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  3.72466 GPa
@Strain 0.730 %,
Temperature -20.0 °C		 540.225 ksi
@Strain 0.730 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  3.97826 GPa
@Strain 0.690 %,
Temperature -40.0 °C		 577.007 ksi
@Strain 0.690 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  10.0 kJ/m² 4.76 ft-lb/in² ISO 180/1A
  8.00 kJ/m²
@Temperature -40.0 °C		 3.81 ft-lb/in²
@Temperature -40.0 °F		 ISO 180/1A
Charpy Impact Unnotched  30.0 J/cm² 143 ft-lb/in² ISO 179/1eU
  25.0 J/cm²
@Temperature -30.0 °C		 119 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.900 J/cm² 4.28 ft-lb/in² ISO 179/1eA
  0.800 J/cm²
@Temperature -30.0 °C		 3.81 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+15 ohm-cm 1.00e+15 ohm-cm IEC 60093
Surface Resistance  >= 1.00e+15 ohm >= 1.00e+15 ohm IEC 60093
Dielectric Constant  3.8
@Frequency 100 Hz		 3.8
@Frequency 100 Hz		 IEC 60250
  3.8
@Frequency 1.00e+6 Hz		 3.8
@Frequency 1.00e+6 Hz		 IEC 60250
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
Melting Point  178 °C 352 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  165 °C 329 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  103 °C 217 °F ISO 75-1/-2
Vicat Softening Point  160 °C 320 °F 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Emissions <8 mg/kg VDA 275
Part Marking Code >POM< ISO 11469
Processing Injection Moulding  
  Other Extrusion  
  Profile Extrusion  
  Sheet Extrusion  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification POM ISO 1043
UL recognition UL  
  UL

POM 的简介 
POM强度、刚度高，弹性好，减磨耐磨性好。其力学性能优异，比强度可达50.5MPa，比刚度可达2650MPa，与金属十分接近。POM的力学性能随温度变化小，共聚POM比均聚POM的变化稍大一点。
POM的冲击强度较高，但常规冲击不及ABS和PC；POM对缺口敏感，有缺口可使冲击强度下降90%之多。
POM的疲劳强度十分突出，10交变载荷作用后，疲劳强度可达35MPa，而PA和PC仅为28MPa。
POM的蠕变性与PA相似，在20℃、21MPa、3000h时仅为2.3%，而且受温度的影响很小。
POM的摩擦因数小，耐磨性好（POM>PA66>PA6>ABS>HPVC>PS>PC），极限PV值很大，自润滑性好。
POM制品对磨时，高载荷作用时易产生类似尖叫的噪声。 
 
POM 化学性质 
POM 按分子链结构不同，聚甲醛可分为均聚甲醛和共聚甲醛，前者密度、结晶度、熔点都高，但是热稳定性差，加工温度窄（10度），对酸堿的稳定性略低；后者密度、结晶度、熔点较低，但热稳定性好，不易分解，加工温度宽（50度）   。
POM 不足之处在于：由受强酸腐蚀，耐侯差，粘合性差，热分解与软化温度接近，限氧指数小。它们广泛用于汽车工业，电子电器，机械设备等。还可以做水龙头、框窗、洗漱盆。
 
POM具有很低的摩擦系数和很好的几何稳定性，特别适合于制作齿轮和轴承。由于它还具有耐高温特性，因此还用于管道器件（管道阀门、泵壳体），草坪设备等。
 
POM 环境性能:   
POM不耐强酸和氧化剂，对烯酸及弱酸有一定的稳定性。
POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。 　　
POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。   
 
应用范围 
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。
 
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生  
手  机：13501802636   
QQ    ：205730283  
邮 箱 ：205730283@qq.com

参考图如下：
3cb92a240a17ac78-f9799ed1752670e2-f5ac6ef2c888142e63826311c7e54689 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-33649.html

免责声明: 本文 POM 311DP NC010,杜邦,易于加工 增强部分性能 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4