  4. POM 500CL NC010,杜邦,具有低磨损和低摩擦

POM 500CL NC010,杜邦,具有低磨损和低摩擦

杜邦高性能聚合物聚甲醛（POM）®500cl NC010乙缩醛 类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋 材料说明：润滑介质粘度缩醛均聚物具有低磨损和低摩擦 聚甲醛是一500cl介质粘度缩醛均聚物树脂含有化学润滑剂专为低磨损和摩擦对金属。
 POM 500CL NC010 的物性表:
 
Physical Properties Metric English Comments
Density  1.41 g/cc 0.0509 lb/in³ ISO 1183
Water Absorption  1.0 %
@Thickness 2.00 mm		 1.0 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.250 %
@Thickness 2.00 mm		 0.250 %
@Thickness 0.0787 in		 Sim. to ISO 62
Linear Mold Shrinkage, Flow  0.019 cm/cm 0.019 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.018 cm/cm 0.018 in/in ISO 294-4 2577
Melt Flow   12 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 12 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 cm³/10min; ISO 1133
  15 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 15 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Hardness, Rockwell M  92 92 ISO 2039-2
Hardness, Rockwell R  120 120 ISO 2039-2
Tensile Stress   9.90 MPa
@Strain 1.10 %,
Temperature 90.0 °C		 1440 psi
@Strain 1.10 %,
Temperature 194 °F		 ISO 11403-1 -2
  25.6 MPa
@Strain 4.60 %,
Temperature 90.0 °C		 3710 psi
@Strain 4.60 %,
Temperature 194 °F		 ISO 11403-1 -2
  27.5 MPa
@Strain 1.40 %,
Temperature 40.0 °C		 3990 psi
@Strain 1.40 %,
Temperature 104 °F		 ISO 11403-1 -2
  28.9 MPa
@Strain 1.10 %,
Temperature 23.0 °C		 4190 psi
@Strain 1.10 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  31.4 MPa
@Strain 8.00 %,
Temperature 90.0 °C		 4550 psi
@Strain 8.00 %,
Temperature 194 °F		 ISO 11403-1 -2
  32.6 MPa
@Strain 11.4 %,
Temperature 90.0 °C		 4730 psi
@Strain 11.4 %,
Temperature 194 °F		 ISO 11403-1 -2
  41.8 MPa
@Strain 1.50 %,
Temperature 0.000 °C		 6060 psi
@Strain 1.50 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  45.7 MPa
@Strain 1.40 %,
Temperature -20.0 °C		 6630 psi
@Strain 1.40 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  52.3 MPa
@Strain 1.60 %,
Temperature -40.0 °C		 7590 psi
@Strain 1.60 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  52.9 MPa
@Strain 5.50 %,
Temperature 40.0 °C		 7670 psi
@Strain 5.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  57.1 MPa
@Strain 9.60 %,
Temperature 40.0 °C		 8280 psi
@Strain 9.60 %,
Temperature 104 °F		 ISO 11403-1 -2
  58.0 MPa
@Strain 4.40 %,
Temperature 23.0 °C		 8410 psi
@Strain 4.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  63.8 MPa
@Strain 7.60 %,
Temperature 23.0 °C		 9250 psi
@Strain 7.60 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  65.0 MPa
@Strain 10.9 %,
Temperature 23.0 °C		 9430 psi
@Strain 10.9 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  70.9 MPa
@Strain 5.80 %,
Temperature 0.000 °C		 10300 psi
@Strain 5.80 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  73.6 MPa
@Strain 10.2 %,
Temperature 0.000 °C		 10700 psi
@Strain 10.2 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  74.1 MPa
@Strain 14.6 %,
Temperature 0.000 °C		 10700 psi
@Strain 14.6 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  78.2 MPa
@Strain 5.50 %,
Temperature -20.0 °C		 11300 psi
@Strain 5.50 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  81.9 MPa
@Strain 9.70 %,
Temperature -20.0 °C		 11900 psi
@Strain 9.70 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  82.2 MPa
@Strain 13.8 %,
Temperature -20.0 °C		 11900 psi
@Strain 13.8 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  93.9 MPa
@Strain 6.40 %,
Temperature -40.0 °C		 13600 psi
@Strain 6.40 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  96.7 MPa
@Strain 11.1 %,
Temperature -40.0 °C		 14000 psi
@Strain 11.1 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  97.1 MPa
@Strain 15.9 %,
Temperature -40.0 °C		 14100 psi
@Strain 15.9 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Tensile Strength, Yield  67.0 MPa 9720 psi ISO 527-1/-2
Elongation at Break  25 % 25 % Nominal; ISO 527-1/-2
Elongation at Yield  15 % 15 % ISO 527-1/-2
Tensile Modulus  3.10 GPa 450 ksi ISO 527-1/-2
Flexural Modulus  2.90 GPa 421 ksi ISO 178
Shear Modulus   0.222 GPa
@Temperature 120 °C		 32.2 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  0.509 GPa
@Temperature 70.0 °C		 73.8 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  0.907 GPa
@Temperature 20.0 °C		 132 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  1.105 GPa
@Temperature -20.0 °C		 160.3 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  1.29 GPa
@Temperature -50.0 °C		 187 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus   0.308163 GPa
@Strain 9.80 %,
Temperature 100 °C		 44.6960 ksi
@Strain 9.80 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.450 GPa
@Strain 8.60 %,
Temperature 80.0 °C		 65.3 ksi
@Strain 8.60 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.498148 GPa
@Strain 5.40 %,
Temperature 100 °C		 72.2514 ksi
@Strain 5.40 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.521818 GPa
@Strain 11.0 %,
Temperature 40.0 °C		 75.6845 ksi
@Strain 11.0 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.632479 GPa
@Strain 11.7 %,
Temperature 0.000 °C		 91.7347 ksi
@Strain 11.7 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  0.737209 GPa
@Strain 4.30 %,
Temperature 80.0 °C		 106.925 ksi
@Strain 4.30 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.74023 GPa
@Strain 8.70 %,
Temperature 23.0 °C		 107.36 ksi
@Strain 8.70 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.745455 GPa
@Strain 11.0 %,
Temperature -20.0 °C		 108.121 ksi
@Strain 11.0 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  0.762205 GPa
@Strain 12.7 %,
Temperature -40.0 °C		 110.550 ksi
@Strain 12.7 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  0.763636 GPa
@Strain 2.20 %,
Temperature 100 °C		 110.758 ksi
@Strain 2.20 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.961818 GPa
@Strain 5.50 %,
Temperature 40.0 °C		 139.502 ksi
@Strain 5.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.22241 GPa
@Strain 5.80 %,
Temperature 0.000 °C		 177.298 ksi
@Strain 5.80 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  1.22727 GPa
@Strain 1.10 %,
Temperature 80.0 °C		 178.003 ksi
@Strain 1.10 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.31818 GPa
@Strain 4.40 %,
Temperature 23.0 °C		 191.189 ksi
@Strain 4.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  1.42182 GPa
@Strain 5.50 %,
Temperature -20.0 °C		 206.221 ksi
@Strain 5.50 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  1.46719 GPa
@Strain 6.40 %,
Temperature -40.0 °C		 212.801 ksi
@Strain 6.40 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  1.96429 GPa
@Strain 1.40 %,
Temperature 40.0 °C		 284.901 ksi
@Strain 1.40 %,
Temperature 104 °F		 ISO 11403-1 -2
  2.62727 GPa
@Strain 1.10 %,
Temperature 23.0 °C		 381.059 ksi
@Strain 1.10 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.78667 GPa
@Strain 1.50 %,
Temperature 0.000 °C		 404.179 ksi
@Strain 1.50 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  3.26429 GPa
@Strain 1.40 %,
Temperature -20.0 °C		 473.453 ksi
@Strain 1.40 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  3.26875 GPa
@Strain 1.60 %,
Temperature -40.0 °C		 474.099 ksi
@Strain 1.60 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  9.00 kJ/m² 4.28 ft-lb/in² ISO 180/1A
  9.00 kJ/m²
@Temperature -40.0 °C		 4.28 ft-lb/in²
@Temperature -40.0 °F		 ISO 180/1A
Charpy Impact Unnotched  35.0 J/cm² 167 ft-lb/in² ISO 179/1eU
  29.0 J/cm²
@Temperature -30.0 °C		 138 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.800 J/cm² 3.81 ft-lb/in² ISO 179/1eA
  0.700 J/cm²
@Temperature -30.0 °C		 3.33 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
 
Electrical Properties Metric English Comments
Surface Resistance  >= 1.00e+15 ohm >= 1.00e+15 ohm IEC 60093
Dielectric Constant   4.1
@Frequency 1.00e+6 Hz		 4.1
@Frequency 1.00e+6 Hz		 IEC 60250
  4.2
@Frequency 100 Hz		 4.2
@Frequency 100 Hz		 IEC 60250
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
Melting Point  178 °C 352 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  158 °C 316 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  90.0 °C 194 °F ISO 75-1/-2
Vicat Softening Point  160 °C 320 °F 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
Flame Spread  28 mm/min
@Thickness 1.00 mm		 1.1 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Part Marking Code >POM< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification POM ISO 1043
UL recognition UL  
  UL
 
POM 的简介 
POM强度、刚度高，弹性好，减磨耐磨性好。其力学性能优异，比强度可达50.5MPa，比刚度可达2650MPa，与金属十分接近。POM的力学性能随温度变化小，共聚POM比均聚POM的变化稍大一点。
POM的冲击强度较高，但常规冲击不及ABS和PC；POM对缺口敏感，有缺口可使冲击强度下降90%之多。
POM的疲劳强度十分突出，10交变载荷作用后，疲劳强度可达35MPa，而PA和PC仅为28MPa。
POM的蠕变性与PA相似，在20℃、21MPa、3000h时仅为2.3%，而且受温度的影响很小。
POM的摩擦因数小，耐磨性好（POM>PA66>PA6>ABS>HPVC>PS>PC），极限PV值很大，自润滑性好。
POM制品对磨时，高载荷作用时易产生类似尖叫的噪声。 
 
POM 化学性质 
POM 按分子链结构不同，聚甲醛可分为均聚甲醛和共聚甲醛，前者密度、结晶度、熔点都高，但是热稳定性差，加工温度窄（10度），对酸堿的稳定性略低；后者密度、结晶度、熔点较低，但热稳定性好，不易分解，加工温度宽（50度）   。
POM 不足之处在于：由受强酸腐蚀，耐侯差，粘合性差，热分解与软化温度接近，限氧指数小。它们广泛用于汽车工业，电子电器，机械设备等。还可以做水龙头、框窗、洗漱盆。
 
POM具有很低的摩擦系数和很好的几何稳定性，特别适合于制作齿轮和轴承。由于它还具有耐高温特性，因此还用于管道器件（管道阀门、泵壳体），草坪设备等。
 
POM 环境性能:   
POM不耐强酸和氧化剂，对烯酸及弱酸有一定的稳定性。
POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。 　　
POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。   

应用范围 
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。
 
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生  
手  机：13501802636   
QQ    ：205730283  
邮 箱 ：205730283@qq.com

参考图如下：
宝理 外包 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-33669.html

免责声明: 本文 POM 500CL NC010,杜邦,具有低磨损和低摩擦 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4