杜邦高性能聚合物聚甲醛（POM）®520mp NC010乙缩醛 类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋 材料说明：20%聚四氟乙烯®润滑介质粘度缩醛均聚物具有低磨损和低摩擦 聚甲醛是一520mp介质粘度缩醛均聚物含有20%聚四氟乙烯PTFE微粉。它是专为需要低磨损和/或摩擦的应用
 POM 520MP NC010 的物性表：
 
Physical Properties Metric English Comments
Density  1.54 g/cc 0.0556 lb/in³ ISO 1183
Linear Mold Shrinkage, Flow  0.019 cm/cm 0.019 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.015 cm/cm 0.015 in/in ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Stress  32.4 MPa
@Strain 1.80 %,
Temperature 23.0 °C		 4700 psi
@Strain 1.80 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  33.3 MPa
@Strain 1.10 %,
Temperature -40.0 °C		 4830 psi
@Strain 1.10 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  38.4 MPa
@Strain 1.70 %,
Temperature 0.000 °C		 5570 psi
@Strain 1.70 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  49.2 MPa
@Strain 7.10 %,
Temperature 23.0 °C		 7140 psi
@Strain 7.10 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  50.2 MPa
@Strain 12.4 %,
Temperature 23.0 °C		 7280 psi
@Strain 12.4 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  50.6 MPa
@Strain 17.8 %,
Temperature 23.0 °C		 7340 psi
@Strain 17.8 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  57.2 MPa
@Strain 6.90 %,
Temperature 0.000 °C		 8300 psi
@Strain 6.90 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  58.2 MPa
@Strain 12.1 %,
Temperature 0.000 °C		 8440 psi
@Strain 12.1 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  58.5 MPa
@Strain 17.3 %,
Temperature 0.000 °C		 8480 psi
@Strain 17.3 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  68.5 MPa
@Strain 4.20 %,
Temperature -40.0 °C		 9940 psi
@Strain 4.20 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  72.6 MPa
@Strain 7.40 %,
Temperature -40.0 °C		 10500 psi
@Strain 7.40 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  73.6 MPa
@Strain 10.5 %,
Temperature -40.0 °C		 10700 psi
@Strain 10.5 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Tensile Strength, Yield  53.0 MPa 7690 psi ISO 527-1/-2
Elongation at Break  15 % 15 % Nominal; ISO 527-1/-2
Elongation at Yield  13 % 13 % ISO 527-1/-2
Tensile Modulus  2.80 GPa 406 ksi ISO 527-1/-2
Flexural Modulus  2.70 GPa 392 ksi ISO 178
Secant Modulus  0.353968 GPa
@Strain 6.30 %,
Temperature 100 °C		 51.3395 ksi
@Strain 6.30 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.354225 GPa
@Strain 14.2 %,
Temperature 23.0 °C		 51.3768 ksi
@Strain 14.2 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.419424 GPa
@Strain 13.9 %,
Temperature 0.000 °C		 60.8333 ksi
@Strain 13.9 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  0.441176 GPa
@Strain 6.80 %,
Temperature 80.0 °C		 63.9882 ksi
@Strain 6.80 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.600 GPa
@Strain 3.10 %,
Temperature 100 °C		 87.0 ksi
@Strain 3.10 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.692958 GPa
@Strain 7.10 %,
Temperature 23.0 °C		 100.507 ksi
@Strain 7.10 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.747059 GPa
@Strain 3.40 %,
Temperature 80.0 °C		 108.353 ksi
@Strain 3.40 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.828986 GPa
@Strain 6.90 %,
Temperature 0.000 °C		 120.236 ksi
@Strain 6.90 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  0.850 GPa
@Strain 0.800 %,
Temperature 100 °C		 123 ksi
@Strain 0.800 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.870238 GPa
@Strain 8.40 %,
Temperature -40.0 °C		 126.219 ksi
@Strain 8.40 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  1.06667 GPa
@Strain 0.900 %,
Temperature 80.0 °C		 154.710 ksi
@Strain 0.900 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.63095 GPa
@Strain 4.20 %,
Temperature -40.0 °C		 236.553 ksi
@Strain 4.20 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  1.80 GPa
@Strain 1.80 %,
Temperature 23.0 °C		 261 ksi
@Strain 1.80 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.25882 GPa
@Strain 1.70 %,
Temperature 0.000 °C		 327.619 ksi
@Strain 1.70 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  3.02727 GPa
@Strain 1.10 %,
Temperature -40.0 °C		 439.075 ksi
@Strain 1.10 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  4.00 kJ/m² 1.90 ft-lb/in² ISO 180/1A
Charpy Impact Unnotched  7.00 J/cm² 33.3 ft-lb/in² ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm² 1.90 ft-lb/in² ISO 179/1eA
  0.400 J/cm²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour  1500 MPa
@Time 3600 sec		 218000 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours  800 MPa
@Time 3.60e+6 sec		 116000 psi
@Time 1000 hour		 ISO 899-1
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  100 µm/m-°C 55.6 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  97.0 µm/m-°C 53.9 µin/in-°F ISO 11359-1/-2
Melting Point  178 °C 352 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  160 °C 320 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  94.0 °C 201 °F ISO 75-1/-2
Flammability, UL94  HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Emission of organic compounds 7.5 µgC/g VDA 277
Part Marking Code >POM-SD20< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification POM-SD20 ISO 1043
UL recognition UL
POM 的简介 
POM强度、刚度高，弹性好，减磨耐磨性好。其力学性能优异，比强度可达50.5MPa，比刚度可达2650MPa，与金属十分接近。POM的力学性能随温度变化小，共聚POM比均聚POM的变化稍大一点。
POM的冲击强度较高，但常规冲击不及ABS和PC；POM对缺口敏感，有缺口可使冲击强度下降90%之多。
POM的疲劳强度十分突出，10交变载荷作用后，疲劳强度可达35MPa，而PA和PC仅为28MPa。
POM的蠕变性与PA相似，在20℃、21MPa、3000h时仅为2.3%，而且受温度的影响很小。
POM的摩擦因数小，耐磨性好（POM>PA66>PA6>ABS>HPVC>PS>PC），极限PV值很大，自润滑性好。
POM制品对磨时，高载荷作用时易产生类似尖叫的噪声。 

POM 化学性质 
POM 按分子链结构不同，聚甲醛可分为均聚甲醛和共聚甲醛，前者密度、结晶度、熔点都高，但是热稳定性差，加工温度窄（10度），对酸堿的稳定性略低；后者密度、结晶度、熔点较低，但热稳定性好，不易分解，加工温度宽（50度）   。
POM 不足之处在于：由受强酸腐蚀，耐侯差，粘合性差，热分解与软化温度接近，限氧指数小。它们广泛用于汽车工业，电子电器，机械设备等。还可以做水龙头、框窗、洗漱盆。
 
POM具有很低的摩擦系数和很好的几何稳定性，特别适合于制作齿轮和轴承。由于它还具有耐高温特性，因此还用于管道器件（管道阀门、泵壳体），草坪设备等。

POM 环境性能:   
POM不耐强酸和氧化剂，对烯酸及弱酸有一定的稳定性。
POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。 　　
POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。   

应用范围 
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生  
手  机：13501802636   
QQ    ：205730283  
邮 箱 ：205730283@qq.com

参考图如下：
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-33708.html

免责声明: 本文 POM 520MP NC010,杜邦,20%聚四氟乙烯®润滑 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4