POM 527UV NC010,杜邦,紫外线稳定介质粘度

杜邦高性能聚合物聚甲醛（POM）®527uv NC010乙缩醛 类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋 材料说明：紫外线稳定介质粘度缩醛均聚物 聚甲醛527uv NC010是介质粘度缩醛均聚物树脂的UV稳定剂用于汽车内饰的应用。它有改善紫外线老化特性和热稳定性
 POM 527UV NC010 的物性表：
 
Physical Properties Metric English Comments
Density  1.42 g/cc 0.0513 lb/in³ ISO 1183
Water Absorption  1.2 %
@Thickness 2.00 mm		 1.2 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.170 %
@Thickness 2.00 mm		 0.170 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   84000 cP
@Shear Rate 5000 1/s,
Temperature 230 °C		 84000 cP
@Shear Rate 5000 1/s,
Temperature 446 °F		 ISO 11403-1 -2
  90000 cP
@Shear Rate 5000 1/s,
Temperature 215 °C		 90000 cP
@Shear Rate 5000 1/s,
Temperature 419 °F		 ISO 11403-1 -2
  97000 cP
@Shear Rate 5000 1/s,
Temperature 200 °C		 97000 cP
@Shear Rate 5000 1/s,
Temperature 392 °F		 ISO 11403-1 -2
  268000 cP
@Shear Rate 500 1/s,
Temperature 230 °C		 268000 cP
@Shear Rate 500 1/s,
Temperature 446 °F		 ISO 11403-1 -2
  306000 cP
@Shear Rate 500 1/s,
Temperature 215 °C		 306000 cP
@Shear Rate 500 1/s,
Temperature 419 °F		 ISO 11403-1 -2
  351000 cP
@Shear Rate 500 1/s,
Temperature 200 °C		 351000 cP
@Shear Rate 500 1/s,
Temperature 392 °F		 ISO 11403-1 -2
Linear Mold Shrinkage, Flow  0.020 cm/cm 0.020 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.019 cm/cm 0.019 in/in ISO 294-4 2577
Melt Flow   13 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 13 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 cm³/10min; ISO 1133
  15 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 15 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Hardness, Rockwell M  92 92 ISO 2039-2
Hardness, Rockwell R  120 120 ISO 2039-2
Tensile Stress   11.4 MPa
@Strain 1.20 %,
Temperature 90.0 °C		 1650 psi
@Strain 1.20 %,
Temperature 194 °F		 ISO 11403-1 -2
  28.0 MPa
@Strain 4.80 %,
Temperature 90.0 °C		 4060 psi
@Strain 4.80 %,
Temperature 194 °F		 ISO 11403-1 -2
  28.0 MPa
@Strain 1.30 %,
Temperature 40.0 °C		 4060 psi
@Strain 1.30 %,
Temperature 104 °F		 ISO 11403-1 -2
  31.4 MPa
@Strain 1.20 %,
Temperature 23.0 °C		 4550 psi
@Strain 1.20 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  32.0 MPa
@Strain 8.50 %,
Temperature 90.0 °C		 4640 psi
@Strain 8.50 %,
Temperature 194 °F		 ISO 11403-1 -2
  32.5 MPa
@Strain 12.1 %,
Temperature 90.0 °C		 4710 psi
@Strain 12.1 %,
Temperature 194 °F		 ISO 11403-1 -2
  35.1 MPa
@Strain 1.00 %,
Temperature -40.0 °C		 5090 psi
@Strain 1.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  42.6 MPa
@Strain 1.20 %,
Temperature 0.000 °C		 6180 psi
@Strain 1.20 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  48.2 MPa
@Strain 1.30 %,
Temperature -20.0 °C		 6990 psi
@Strain 1.30 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  54.0 MPa
@Strain 5.00 %,
Temperature 40.0 °C		 7830 psi
@Strain 5.00 %,
Temperature 104 °F		 ISO 11403-1 -2
  57.8 MPa
@Strain 8.80 %,
Temperature 40.0 °C		 8380 psi
@Strain 8.80 %,
Temperature 104 °F		 ISO 11403-1 -2
  58.5 MPa
@Strain 11.5 %,
Temperature 40.0 °C		 8480 psi
@Strain 11.5 %,
Temperature 104 °F		 ISO 11403-1 -2
  61.1 MPa
@Strain 4.90 %,
Temperature 23.0 °C		 8860 psi
@Strain 4.90 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  66.4 MPa
@Strain 8.60 %,
Temperature 23.0 °C		 9630 psi
@Strain 8.60 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  67.5 MPa
@Strain 12.3 %,
Temperature 23.0 °C		 9790 psi
@Strain 12.3 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  68.8 MPa
@Strain 4.80 %,
Temperature 0.000 °C		 9980 psi
@Strain 4.80 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  72.7 MPa
@Strain 8.40 %,
Temperature 0.000 °C		 10500 psi
@Strain 8.40 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  73.5 MPa
@Strain 12.0 %,
Temperature 0.000 °C		 10700 psi
@Strain 12.0 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  79.5 MPa
@Strain 5.20 %,
Temperature -20.0 °C		 11500 psi
@Strain 5.20 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  83.1 MPa
@Strain 9.10 %,
Temperature -20.0 °C		 12100 psi
@Strain 9.10 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  84.0 MPa
@Strain 13.0 %,
Temperature -20.0 °C		 12200 psi
@Strain 13.0 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  87.3 MPa
@Strain 4.00 %,
Temperature -40.0 °C		 12700 psi
@Strain 4.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  97.7 MPa
@Strain 7.00 %,
Temperature -40.0 °C		 14200 psi
@Strain 7.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  99.1 MPa
@Strain 10.0 %,
Temperature -40.0 °C		 14400 psi
@Strain 10.0 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Tensile Strength, Yield  70.0 MPa 10200 psi ISO 527-1/-2
Elongation at Break  30 % 30 % Nominal; ISO 527-1/-2
Elongation at Yield  17 % 17 % ISO 527-1/-2
Tensile Modulus  3.10 GPa 450 ksi ISO 527-1/-2
Flexural Modulus  3.00 GPa 435 ksi ISO 178
Shear Modulus   0.2554 GPa
@Temperature 120 °C		 37.04 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  0.5689 GPa
@Temperature 70.0 °C		 82.51 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  0.9834 GPa
@Temperature 20.0 °C		 142.6 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  1.2147 GPa
@Temperature -20.0 °C		 176.18 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  1.3839 GPa
@Temperature -50.0 °C		 200.72 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus   0.357143 GPa
@Strain 8.40 %,
Temperature 100 °C		 51.8000 ksi
@Strain 8.40 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.450 GPa
@Strain 8.40 %,
Temperature 80.0 °C		 65.3 ksi
@Strain 8.40 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.588095 GPa
@Strain 4.20 %,
Temperature 100 °C		 85.2973 ksi
@Strain 4.20 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.644444 GPa
@Strain 9.00 %,
Temperature 40.0 °C		 93.4702 ksi
@Strain 9.00 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.684694 GPa
@Strain 9.80 %,
Temperature 23.0 °C		 99.3080 ksi
@Strain 9.80 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.750 GPa
@Strain 4.20 %,
Temperature 80.0 °C		 109 ksi
@Strain 4.20 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.760417 GPa
@Strain 9.60 %,
Temperature 0.000 °C		 110.291 ksi
@Strain 9.60 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  0.802885 GPa
@Strain 10.4 %,
Temperature -20.0 °C		 116.450 ksi
@Strain 10.4 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  0.980 GPa
@Strain 1.00 %,
Temperature 100 °C		 142 ksi
@Strain 1.00 %,
Temperature 212 °F		 ISO 11403-1 -2
  1.08 GPa
@Strain 5.00 %,
Temperature 40.0 °C		 157 ksi
@Strain 5.00 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.10 GPa
@Strain 1.10 %,
Temperature 80.0 °C		 160 ksi
@Strain 1.10 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.22875 GPa
@Strain 8.00 %,
Temperature -40.0 °C		 178.218 ksi
@Strain 8.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  1.24694 GPa
@Strain 4.90 %,
Temperature 23.0 °C		 180.856 ksi
@Strain 4.90 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  1.43333 GPa
@Strain 4.80 %,
Temperature 0.000 °C		 207.890 ksi
@Strain 4.80 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  1.52885 GPa
@Strain 5.20 %,
Temperature -20.0 °C		 221.744 ksi
@Strain 5.20 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  2.15385 GPa
@Strain 1.30 %,
Temperature 40.0 °C		 312.394 ksi
@Strain 1.30 %,
Temperature 104 °F		 ISO 11403-1 -2
  2.1825 GPa
@Strain 4.00 %,
Temperature -40.0 °C		 316.55 ksi
@Strain 4.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.61667 GPa
@Strain 1.20 %,
Temperature 23.0 °C		 379.522 ksi
@Strain 1.20 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  3.51 GPa
@Strain 1.00 %,
Temperature -40.0 °C		 509 ksi
@Strain 1.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  3.55 GPa
@Strain 1.20 %,
Temperature 0.000 °C		 515 ksi
@Strain 1.20 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  3.70769 GPa
@Strain 1.30 %,
Temperature -20.0 °C		 537.763 ksi
@Strain 1.30 %,
Temperature -4.00 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  8.00 kJ/m² 3.81 ft-lb/in² ISO 180/1A
  8.00 kJ/m²
@Temperature -40.0 °C		 3.81 ft-lb/in²
@Temperature -40.0 °F		 ISO 180/1A
Charpy Impact Unnotched  26.0 J/cm² 124 ft-lb/in² ISO 179/1eU
  26.0 J/cm²
@Temperature -30.0 °C		 124 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.900 J/cm² 4.28 ft-lb/in² ISO 179/1eA
  0.800 J/cm²
@Temperature -30.0 °C		 3.81 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+13 ohm-cm 1.00e+13 ohm-cm IEC 60093
Dielectric Constant   3.5
@Frequency 100 Hz		 3.5
@Frequency 100 Hz		 IEC 60250
  3.8
@Frequency 1.00e+6 Hz		 3.8
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  120 µm/m-°C 66.7 µin/in-°F ISO 11359-1/-2
Melting Point  178 °C 352 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  163 °C 325 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  95.0 °C 203 °F ISO 75-1/-2
Vicat Softening Point  160 °C 320 °F 50°C/h 50N; ISO 306
Flammability, UL94  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Part Marking Code >POM< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification POM ISO 1043
Special characteristics Light stabilised or stable to light  
  U.V. stabilised or stable to weather  
UL recognition UL
 
POM 的简介 
 
POM强度、刚度高，弹性好，减磨耐磨性好。其力学性能优异，比强度可达50.5MPa，比刚度可达2650MPa，与金属十分接近。POM的力学性能随温度变化小，共聚POM比均聚POM的变化稍大一点。
POM的冲击强度较高，但常规冲击不及ABS和PC；POM对缺口敏感，有缺口可使冲击强度下降90%之多。
POM的疲劳强度十分突出，10交变载荷作用后，疲劳强度可达35MPa，而PA和PC仅为28MPa。
POM的蠕变性与PA相似，在20℃、21MPa、3000h时仅为2.3%，而且受温度的影响很小。
POM的摩擦因数小，耐磨性好（POM>PA66>PA6>ABS>HPVC>PS>PC），极限PV值很大，自润滑性好。
POM制品对磨时，高载荷作用时易产生类似尖叫的噪声。 
 
POM 化学性质 
POM 按分子链结构不同，聚甲醛可分为均聚甲醛和共聚甲醛，前者密度、结晶度、熔点都高，但是热稳定性差，加工温度窄（10度），对酸堿的稳定性略低；后者密度、结晶度、熔点较低，但热稳定性好，不易分解，加工温度宽（50度）   。
POM 不足之处在于：由受强酸腐蚀，耐侯差，粘合性差，热分解与软化温度接近，限氧指数小。它们广泛用于汽车工业，电子电器，机械设备等。还可以做水龙头、框窗、洗漱盆。
 
POM具有很低的摩擦系数和很好的几何稳定性，特别适合于制作齿轮和轴承。由于它还具有耐高温特性，因此还用于管道器件（管道阀门、泵壳体），草坪设备等。
 
POM 环境性能:   
POM不耐强酸和氧化剂，对烯酸及弱酸有一定的稳定性。
POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。 　　
POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。   
 
应用范围 
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。
 
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生  
手  机：13501802636   
QQ    ：205730283  
邮 箱 ：205730283@qq.com

参考图如下：
3cb92a240a17ac78-f9799ed1752670e2-ad078d8db898ff960bebdb73707ba315 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-33720.html

免责声明: 本文 POM 527UV NC010,杜邦,紫外线稳定介质粘度 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4