POM FG511DP,杜邦,提高热稳定性和更精确成型

杜邦高性能聚合物聚甲醛（POM）®fg511dp NC010乙缩醛 类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋 材料说明：用于食品接触应用程序开发的核介质粘度缩醛均聚物
 POM FG511DP 的物性表：
 
Physical Properties Metric English Comments
Density  1.42 g/cc 0.0513 lb/in³ ISO 1183
Water Absorption  0.90 %
@Thickness 2.00 mm		 0.90 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.200 %
@Thickness 2.00 mm		 0.200 %
@Thickness 0.0787 in		 Sim. to ISO 62
Linear Mold Shrinkage, Flow  0.019 cm/cm 0.019 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.018 cm/cm 0.018 in/in ISO 294-4 2577
Melt Flow   13 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 13 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 cm³/10min; ISO 1133
  14 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 14 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Stress   15.4 MPa
@Strain 0.500 %,
Temperature 23.0 °C		 2230 psi
@Strain 0.500 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  17.8 MPa
@Strain 0.500 %,
Temperature 0.000 °C		 2580 psi
@Strain 0.500 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  21.0 MPa
@Strain 0.500 %,
Temperature -40.0 °C		 3050 psi
@Strain 0.500 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  50.3 MPa
@Strain 2.20 %,
Temperature 23.0 °C		 7300 psi
@Strain 2.20 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  56.4 MPa
@Strain 2.20 %,
Temperature 0.000 °C		 8180 psi
@Strain 2.20 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  63.0 MPa
@Strain 3.80 %,
Temperature 23.0 °C		 9140 psi
@Strain 3.80 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  67.8 MPa
@Strain 2.00 %,
Temperature -40.0 °C		 9830 psi
@Strain 2.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  68.8 MPa
@Strain 6.00 %,
Temperature 23.0 °C		 9980 psi
@Strain 6.00 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  70.7 MPa
@Strain 3.80 %,
Temperature 0.000 °C		 10300 psi
@Strain 3.80 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  75.1 MPa
@Strain 5.00 %,
Temperature 0.000 °C		 10900 psi
@Strain 5.00 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  88.3 MPa
@Strain 3.60 %,
Temperature -40.0 °C		 12800 psi
@Strain 3.60 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  94.6 MPa
@Strain 5.00 %,
Temperature -40.0 °C		 13700 psi
@Strain 5.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Tensile Strength, Yield  73.0 MPa 10600 psi ISO 527-1/-2
Elongation at Break  25 % 25 % Nominal; ISO 527-1/-2
Elongation at Yield  12 % 12 % ISO 527-1/-2
Tensile Modulus  3.40 GPa 493 ksi ISO 527-1/-2
Flexural Strength  87.0 MPa
@Strain 3.50 %		 12600 psi
@Strain 3.50 %		 ISO 178
Flexural Modulus  3.20 GPa 464 ksi ISO 178
Secant Modulus   0.365 GPa
@Strain 8.00 %,
Temperature 100 °C		 52.9 ksi
@Strain 8.00 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.575 GPa
@Strain 4.80 %,
Temperature 100 °C		 83.4 ksi
@Strain 4.80 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.636667 GPa
@Strain 6.00 %,
Temperature 80.0 °C		 92.3422 ksi
@Strain 6.00 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.746875 GPa
@Strain 3.20 %,
Temperature 100 °C		 108.327 ksi
@Strain 3.20 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.87875 GPa
@Strain 8.00 %,
Temperature 23.0 °C		 127.45 ksi
@Strain 8.00 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.889474 GPa
@Strain 3.80 %,
Temperature 80.0 °C		 129.009 ksi
@Strain 3.80 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.975 GPa
@Strain 1.60 %,
Temperature 100 °C		 141 ksi
@Strain 1.60 %,
Temperature 212 °F		 ISO 11403-1 -2
  1.11429 GPa
@Strain 7.00 %,
Temperature 0.000 °C		 161.617 ksi
@Strain 7.00 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  1.15 GPa
@Strain 0.400 %,
Temperature 100 °C		 167 ksi
@Strain 0.400 %,
Temperature 212 °F		 ISO 11403-1 -2
  1.23158 GPa
@Strain 1.90 %,
Temperature 80.0 °C		 178.628 ksi
@Strain 1.90 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.38429 GPa
@Strain 7.00 %,
Temperature -40.0 °C		 200.777 ksi
@Strain 7.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  1.48636 GPa
@Strain 4.40 %,
Temperature 23.0 °C		 215.582 ksi
@Strain 4.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  1.60 GPa
@Strain 0.400 %,
Temperature 80.0 °C		 232 ksi
@Strain 0.400 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.66591 GPa
@Strain 4.40 %,
Temperature 0.000 °C		 241.624 ksi
@Strain 4.40 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.22927 GPa
@Strain 4.10 %,
Temperature -40.0 °C		 323.333 ksi
@Strain 4.10 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.28636 GPa
@Strain 2.20 %,
Temperature 23.0 °C		 331.614 ksi
@Strain 2.20 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.56364 GPa
@Strain 2.20 %,
Temperature 0.000 °C		 371.830 ksi
@Strain 2.20 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  3.08 GPa
@Strain 0.500 %,
Temperature 23.0 °C		 447 ksi
@Strain 0.500 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  3.39 GPa
@Strain 2.00 %,
Temperature -40.0 °C		 492 ksi
@Strain 2.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  3.56 GPa
@Strain 0.500 %,
Temperature 0.000 °C		 516 ksi
@Strain 0.500 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  4.20 GPa
@Strain 0.500 %,
Temperature -40.0 °C		 609 ksi
@Strain 0.500 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Charpy Impact Unnotched  22.0 J/cm² 105 ft-lb/in² ISO 179/1eU
  20.0 J/cm²
@Temperature -30.0 °C		 95.2 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.700 J/cm² 3.33 ft-lb/in² ISO 179/1eA
  0.650 J/cm²
@Temperature -30.0 °C		 3.09 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  100 µm/m-°C 55.6 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
Melting Point  178 °C 352 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  163 °C 325 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  107 °C 225 °F ISO 75-1/-2
Vicat Softening Point  160 °C 320 °F 50°C/h 50N; ISO 306
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Part Marking Code >POM< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification POM ISO 1043
 
POM 的简介 
聚甲醛是一种表面光滑，有光泽的硬而致密的材料，淡黄或白色，可在-40- 100°C温度范围内长期使用。它的耐磨性和自润滑性也比绝大多数工程塑料优越，又有良好的耐油，耐过氧化物性能。很不耐酸，不耐强碱和不耐紫外线的辐射。
 
POM 物理性质
聚甲醛的拉伸强度达70MPa，吸水性小，尺寸稳定，有光泽，这些性能都比尼龙好，聚甲醛为高度结晶的树脂，在热塑性树脂中是最坚韧的。具抗热强度，弯曲强度，耐疲劳性强度均高，耐磨性和电性能优良。
 
POM 聚甲醛的性能:   
  性 能 数 值   
  比重 1.43  
  熔点 175°C    
  伸强度（屈服） 70MPa   
  伸长率（屈服） 15%  
  （断裂） 15%   
  冲击强度（无缺口） 108KJ/m2  
  （带缺口） 7.6KJ/m2
 
应用范围 
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生  
手  机：13501802636   
QQ    ：205730283  
邮 箱 ：205730283@qq.com

参考图如下：
04cf2c76bac770c4-becabf6d49eef1bc-0db4e6a50ea02d784af7d52301fd0e18 


转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-33786.html

免责声明: 本文 POM FG511DP,杜邦,提高热稳定性和更精确成型 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4