| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | ASTM D792 | ||
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.80 % | 0.80 % | ISO 62 | ||
| Moisture Absorption | 0.200 % | 0.200 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 | ||
| 0.0040 cm/cm | 0.0040 in/in | ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | ISO 294-4 | ||
| 0.014 cm/cm | 0.014 in/in | ASTM D955 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 106 MPa | 15400 psi | 5mm/min; ISO 527-2/1A | ||
| 110 MPa | 16000 psi | ASTM D638 | |||
| 68.9 MPa @Temperature 71.1 °C |
10000 psi @Temperature 160 °F |
ASTM D638 | |||
| 159 MPa @Temperature -40.0 °C |
23000 psi @Temperature -40.0 °F |
ASTM D638 | |||
| Elongation at Break | 2.0 % | 2.0 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 8.60 GPa | 1250 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 | ||
| Flexural Modulus | 8.70 GPa | 1260 ksi | ISO 178 | ||
| 3.45 GPa @Temperature 104 °C |
500 ksi @Temperature 220 °F |
ASTM D790 | |||
| 4.83 GPa @Temperature 71.1 °C |
700 ksi @Temperature 160 °F |
ASTM D790 | |||
| 7.58 GPa @Temperature 22.8 °C |
1100 ksi @Temperature 73.0 °F |
ASTM D790 | |||
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 | ||
| 0.374 J/cm @Temperature -40.0 °C |
0.700 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |||
| 0.481 J/cm @Temperature 82.2 °C |
0.900 ft-lb/in @Temperature 180 °F |
ASTM D256 | |||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO 179/1eU | ||
| 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.640 J/cm² | 3.05 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.36e+14 ohm-cm | 1.36e+14 ohm-cm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 165 °C | 329 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 166 °C | 331 °F | ASTM D3418 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ISO 75-1, -2 | ||
| 163 °C | 325 °F | ASTM D648 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 90.0 - 120 °C | 194 - 248 °F | Cavity temperature | ||
| Zone 1 | 170 - 180 °C | 338 - 356 °F | |||
| Zone 2 | 180 - 190 °C | 356 - 374 °F | |||
| Zone 3 | 180 - 190 °C | 356 - 374 °F | |||
| Zone 4 | 190 - 200 °C | 374 - 392 °F | |||
| Die Temperature | 190 - 200 °C | 374 - 392 °F | |||
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |||
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Dry Time | 3.00 hour | 3.00 hour | |||
| Injection Pressure | 90.0 - 140 MPa | 13100 - 20300 psi | |||
| Hold Pressure | 90.0 - 140 MPa | 13100 - 20300 psi | |||
| Back Pressure | 0.500 MPa | 72.5 psi | |||
| Hot-Working Temperature | 180 - 200 °C | 356 - 392 °F | |||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | slow | ||||
| Pellets | Yes | ||||
| Pre-drying | Drying is not normally required with proper storage | ||||
| Processing conditions | ISO 9988-2 | ||||
| Profile extrusion | Yes | ||||
POM 的简介
聚甲醛是一种表面光滑，有光泽的硬而致密的材料，淡黄或白色，可在-40- 100°C温度范围内长期使用。它的耐磨性和自润滑性也比绝大多数工程塑料优越，又有良好的耐油，耐过氧化物性能。很不耐酸，不耐强碱和不耐紫外线的辐射。
POM 物理性质
聚甲醛的拉伸强度达70MPa，吸水性小，尺寸稳定，有光泽，这些性能都比尼龙好，聚甲醛为高度结晶的树脂，在热塑性树脂中是最坚韧的。具抗热强度，弯曲强度，耐疲劳性强度均高，耐磨性和电性能优良。
POM 聚甲醛的性能:
性 能 数 值
比重 1.43
熔点 175°C
伸强度（屈服） 70MPa
伸长率（屈服） 15%
（断裂） 15%
冲击强度（无缺口） 108KJ/m2
（带缺口） 7.6KJ/m2
应用范围
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。