| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ISO 294-4 | ||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
(MVR) cm³/10min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50mm/min; ISO 527-2/1A | ||
| Elongation at Yield | 9.5 % | 9.5 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 2.60 GPa | 377 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Modulus | 2.56 GPa | 371 ksi | ISO 178 | ||
| Charpy Impact, Notched | 0.640 J/cm² | 3.05 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 167 °C | 333 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-1, -2 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | ||
| Zone 1 | 165 - 175 °C | 329 - 347 °F | |||
| Zone 2 | 170 - 180 °C | 338 - 356 °F | |||
| Zone 3 | 170 - 180 °C | 338 - 356 °F | |||
| Zone 4 | 175 - 185 °C | 347 - 365 °F | |||
| Die Temperature | 180 - 190 °C | 356 - 374 °F | |||
| Melt Temperature | 180 - 190 °C | 356 - 374 °F | |||
| Drying Temperature | 140 °C | 284 °F | |||
| Dry Time | 2.00 hour | 2.00 hour | |||
| Injection Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Hold Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Back Pressure | 0.500 MPa | 72.5 psi | |||
| Hot-Working Temperature | 180 - 200 °C | 356 - 392 °F | |||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | slow-medium | ||||
| Pre-drying | Drying is recommended to obtain optimum emission performance. | ||||
| Profile extrusion | Yes | ||||
| Recommmended shot size | half the maximum shot size | to ensure short residence time. | |||
| Sheet extrusion | No | ||||