类别：聚合物；热塑性；聚甲醛（POM）；乙缩醛共聚物，影响改性
材料说明：Ultraform n2640 Z4 UNC q600是一种高韧性，弹性体的改性POM注塑级。
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.80 % | 0.80 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.019 cm/cm | 0.019 in/in | ASTM Data; MD | ||
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | ISO Data | ||
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ISO Data | ||
| Melt Flow | 5.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
5.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | 50mm/min; ISO 527 | ||
| 44.0 MPa | 6380 psi | 2 in/min; ASTM Test | |||
| 22.0 MPa @Temperature 80.0 °C |
3190 psi @Temperature 176 °F |
ISO Data | |||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| Elongation at Yield | 14 % | 14 % | 50mm/min; ISO 527 | ||
| 14 % | 14 % | 2 in/min; ASTM Test | |||
| 17 % @Temperature 80.0 °C |
17 % @Temperature 176 °F |
ISO Data | |||
| Tensile Modulus | 1.66 GPa | 241 ksi | ASTM Test | ||
| 1.70 GPa | 247 ksi | 1mm/min; ISO 527 | |||
| Flexural Modulus | 1.66 GPa | 241 ksi | ASTM Test | ||
| Izod Impact, Notched | 0.907 J/cm @Temperature -40.0 °C |
1.70 ft-lb/in @Temperature -40.0 °F |
ASTM Test | ||
| 1.49 J/cm @Thickness 3.17 mm |
2.79 ft-lb/in @Thickness 0.125 in |
ASTM Test | |||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| 30.0 J/cm² @Temperature -30.0 °C |
143 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |||
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179 | ||
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |||
| Tensile Creep Modulus, 1 hour | 1350 MPa | 196000 psi | ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 1000 MPa | 145000 psi | ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 4.2 @Frequency 100 Hz |
4.2 @Frequency 100 Hz |
IEC 60250 | ||
| 4.2 @Frequency 1.00e+6 Hz |
4.2 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.011 @Frequency 100 Hz |
0.011 @Frequency 100 Hz |
IEC 60250 | ||
| 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 70.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM Test | ||
| CTE, linear, Parallel to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359 | ||
| Melting Point | 167 °C | 333 °F | 10 K/min | ||
| 167 °C | 333 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ASTM Test | ||
| 140 °C | 284 °F | ISO 75 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75 | ||
| 77.0 °C | 171 °F | ASTM Test | |||
| Vicat Softening Point | 130 °C | 266 °F | (50 °C/h / 50N) - B/50; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|||
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||