类别：聚合物；热塑性；聚甲醛（POM）
材料说明：本®Edgetek工程热塑性化合物组合，涵盖范围广泛的标准和定制的配制高性能材料。此组合包括高温材料的高温环境下，高模量/结构材料的承重和高强度的应用和阻燃产品。这些化合物是根据选定的工程热塑性树脂，复合材料，如碳纤维，玻璃纤维和玻璃珠增强添加剂。
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 | ||
| Water Absorption | 0.20 % @Thickness 3.18 mm |
0.20 % @Thickness 0.125 in |
@ 24 hrs; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.020 - 0.022 cm/cm | 0.020 - 0.022 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 60.7 MPa | 8800 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 8.0 - 10 % | 8.0 - 10 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 3.00 GPa | 435 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 | ||
| Flexural Modulus | 2.52 GPa | 365 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.690 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.29 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C @Thickness 3.18 mm |
230 °F @Thickness 0.125 in |
Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 204 - 227 °C | 399 - 441 °F | |||
| De |
|||||
| Features | Copolymer | ||||
| General Purpose | |||||
| Forms | Pellets | ||||
| Generic Material | Acetal (POM) Copolymer | ||||
| Generic Name | Acetal (POM) Copolymer | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| South America | |||||
| Uses | Automotive Applications | ||||
| Consumer Applications | |||||
| Industrial Applications | |||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com