| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.190 % | 0.190 % | 50% RH, 24 hrs; ASTM D570 |
| 0.270 % | 0.270 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 99.0 MPa | 14400 psi | 5 mm/min; ISO 527 |
| 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 4.3 % | 4.3 % | 5 mm/min; ISO 527 |
| 5.0 % | 5.0 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 5 mm/min; ISO 527 |
| 4.8 % | 4.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.34 GPa | 629 ksi | 1 mm/min; ISO 527 |
| 4.66 GPa | 676 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 155 MPa | 22500 psi | ISO 178 |
| Flexural Modulus | 4.31 GPa | 625 ksi | 2 mm/min; ISO 178 |
| 4.59 GPa | 666 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.340 J/cm | 0.637 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.85 J/cm | 9.09 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 2.0 - 4.0 ohm | 2.0 - 4.0 ohm | ASTM D257 |
| Shielding Effectiveness | 60 dB @Thickness 2.50 mm |
60 dB @Thickness 0.0984 in |
SABIC Method |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 44.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
24.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 190 °C @Thickness 3.20 mm |
374 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 180 °C @Thickness 3.20 mm |
356 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
PEI ES003E 图：