| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 | ||
| Water Absorption | 7.0 % | 7.0 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 149 cm³/g | 149 cm³/g | Viscosity number | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 122 MPa | 17700 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.5 % | 2.5 % | 5mm/min; ISO 527 | ||
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | ISO Test | ||
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 33.0 µm/m-°C | 18.3 µin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C | 41.7 µin/in-°F | ISO 11359 | ||
| Melting Point | 260 °C | 500 °F | 10 K/min | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 1.66 mm |
HB @Thickness 0.0654 in |
|||
| HB @Thickness 0.810 mm |
HB @Thickness 0.0319 in |
||||
| De |
|||||
| Color | BK00564 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
PA66塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。
下图仅供参考（非实物图）：
应用：广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。