类别：聚合物；热塑性塑料；树脂聚合物；丙烯腈-丁二烯-苯乙烯（尼龙）/尼龙共混物，玻璃增强；尼龙
材料说明：®Terblend N ng-02 EF是玻璃纤维增强的紫外线稳定ABS／PA具有良好的尺寸稳定性和高的共混物的冲击强度。流动性的增强使优良的加工性能和表面外观。
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | 23°C/50% RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ISO 2577 | ||
| Melt Flow | 44.8 g/10 min @Load 10.0 kg, Temperature 240 °C |
44.8 g/10 min @Load 22.0 lb, Temperature 464 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell L | 78 | 78 | ISO 2039-2 | ||
| Ball Indentation Hardness | 99.0 MPa @Load 36.5 kg, Time 30.0 sec |
14400 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 | ||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527-1/-2 | ||
| Elongation at Break | 6.0 % | 6.0 % | Nominal, 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 3.10 GPa | 450 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 85.0 MPa | 12300 psi | ISO 178 | ||
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A | ||
| 12.0 kJ/m² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |||
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
| 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| Dissipation Factor | 0.018 @Frequency 1.00e+6 Hz |
0.018 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
33.3 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 118 °C | 244 °F | VST/B/50; ISO 306 | ||
| 200 °C | 392 °F | VST/A/50; ISO 306 | |||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding | ||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection Molding | ||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | Europe | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com