| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Melt Flow | 46 g/10 min | 46 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | |
| Elongation at Break | 20 % | 20 % | |
| Elongation at Yield | 4.0 % | 4.0 % | |
| Modulus of Elasticity | 2.20 GPa | 319 ksi | |
| Charpy Impact Unnotched | 11.5 J/cm² | 54.7 ft-lb/in² | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | |
| Tensile Impact Strength | 42.0 kJ/m² | 20.0 ft-lb/in² | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 3.00e+14 ohm | 3.00e+14 ohm | |
| Dielectric Constant | 2.0 @Frequency 100 Hz |
2.0 @Frequency 100 Hz |
|
| 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 41.0 kV/mm | 1040 kV/in | |
| Dissipation Factor | 0.00080 @Frequency 1e+6 Hz |
0.00080 @Frequency 1e+6 Hz |
|
| 0.00090 @Frequency 100 Hz |
0.00090 @Frequency 100 Hz |
||
| Comparative Tracking Index | 400 V | 400 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | |
| Vicat Softening Point | 116 °C | 241 °F | 50°C/hr/50 N |