PA612 美国杜邦77G33L NC010矿物增强 注塑级

PA612 美国杜邦 77G33L NC010 矿物增强 注塑级
 参考图片：

颗粒图片：

包装图片：

成品图片：
f99c6df6dda12fe1_1

 

 

 
Physical Properties Metric English Comments
Density  1.32 g/cc 0.0477 lb/in³ DAM; ISO 1183
Water Absorption  1.8 %
@Thickness 2.00 mm		 1.8 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  0.700 %
@Thickness 2.00 mm		 0.700 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Water Absorption at Saturation  0.30 % 0.30 % DAM; Immersion 24h; ASTM D570
Viscosity   39840 cP
@Shear Rate 5000 1/s,
Temperature 280 °C		 39840 cP
@Shear Rate 5000 1/s,
Temperature 536 °F		 ISO 11403-1 -2
  100800 cP
@Shear Rate 500 1/s,
Temperature 280 °C		 100800 cP
@Shear Rate 500 1/s,
Temperature 536 °F		 ISO 11403-1 -2
Viscosity Test  100 cm³/g 100 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in DAM; ISO 294-4 2577
  0.0020 cm/cm
@Thickness 3.20 mm		 0.0020 in/in
@Thickness 0.126 in		 DAM
Linear Mold Shrinkage, Transverse  0.0090 cm/cm 0.0090 in/in DAM; ISO 294-4 2577
  0.010 cm/cm
@Thickness 3.20 mm		 0.010 in/in
@Thickness 0.126 in		 DAM; ASTM D149
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  140 MPa 20300 psi 50%RH; ISO 527-1/-2
  168 MPa 24400 psi DAM; ISO 527-1/-2
Tensile Stress   11.79 MPa
@Strain 0.300 %,
Temperature 150 °C		 1710 psi
@Strain 0.300 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  11.8 MPa
@Strain 0.300 %,
Temperature 150 °C		 1710 psi
@Strain 0.300 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  32.0 MPa
@Strain 1.00 %,
Temperature 150 °C		 4640 psi
@Strain 1.00 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  35.55 MPa
@Strain 1.00 %,
Temperature 150 °C		 5156 psi
@Strain 1.00 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  36.8 MPa
@Strain 0.500 %,
Temperature 23.0 °C		 5340 psi
@Strain 0.500 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  39.3 MPa
@Strain 1.40 %,
Temperature 150 °C		 5700 psi
@Strain 1.40 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  41.76 MPa
@Strain 1.30 %,
Temperature 150 °C		 6057 psi
@Strain 1.30 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  46.2 MPa
@Strain 1.90 %,
Temperature 150 °C		 6700 psi
@Strain 1.90 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  46.6 MPa
@Strain 0.500 %,
Temperature 0.000 °C		 6760 psi
@Strain 0.500 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  46.71 MPa
@Strain 1.60 %,
Temperature 150 °C		 6775 psi
@Strain 1.60 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  55.9 MPa
@Strain 0.600 %,
Temperature 23.0 °C		 8110 psi
@Strain 0.600 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  59.047 MPa
@Strain 0.600 %,
Temperature -40.0 °C		 8564.1 psi
@Strain 0.600 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  66.51 MPa
@Strain 4.40 %,
Temperature 150 °C		 9646 psi
@Strain 4.40 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  68.3 MPa
@Strain 0.700 %,
Temperature -40.0 °C		 9910 psi
@Strain 0.700 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  73.04 MPa
@Strain 0.800 %,
Temperature 0.000 °C		 10590 psi
@Strain 0.800 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  80.0 MPa
@Strain 1.20 %,
Temperature 23.0 °C		 11600 psi
@Strain 1.20 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  81.1 MPa
@Strain 0.900 %,
Temperature 0.000 °C		 11800 psi
@Strain 0.900 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  88.05 MPa
@Strain 1.00 %,
Temperature 23.0 °C		 12770 psi
@Strain 1.00 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  114.35 MPa
@Strain 1.40 %,
Temperature 23.0 °C		 16585 psi
@Strain 1.40 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  114.9 MPa
@Strain 1.40 %,
Temperature 0.000 °C		 16660 psi
@Strain 1.40 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  120.51 MPa
@Strain 1.40 %,
Temperature 0.000 °C		 17479 psi
@Strain 1.40 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  124.03 MPa
@Strain 1.40 %,
Temperature -40.0 °C		 17989 psi
@Strain 1.40 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  127.3 MPa
@Strain 2.50 %,
Temperature 23.0 °C		 18460 psi
@Strain 2.50 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  130.25 MPa
@Strain 1.70 %,
Temperature 23.0 °C		 18891 psi
@Strain 1.70 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  135.7 MPa
@Strain 2.90 %,
Temperature 23.0 °C		 19680 psi
@Strain 2.90 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  146.5 MPa
@Strain 2.00 %,
Temperature 0.000 °C		 21250 psi
@Strain 2.00 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  147.6 MPa
@Strain 1.80 %,
Temperature -40.0 °C		 21410 psi
@Strain 1.80 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  149.87 MPa
@Strain 1.80 %,
Temperature -40.0 °C		 21737 psi
@Strain 1.80 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  161.25 MPa
@Strain 2.10 %,
Temperature 0.000 °C		 23387 psi
@Strain 2.10 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  167.76 MPa
@Strain 2.10 %,
Temperature -40.0 °C		 24332 psi
@Strain 2.10 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  169.5 MPa
@Strain 3.00 %,
Temperature 23.0 °C		 24580 psi
@Strain 3.00 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  178.45 MPa
@Strain 2.50 %,
Temperature 0.000 °C		 25882 psi
@Strain 2.50 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  188.1 MPa
@Strain 2.50 %,
Temperature -40.0 °C		 27280 psi
@Strain 2.50 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  211.6 MPa
@Strain 3.00 %,
Temperature -40.0 °C		 30690 psi
@Strain 3.00 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
Elongation at Break  3.2 % 3.2 % DAM; ISO 527-1/-2
  3.2 % 3.2 % 50%RH; ISO 527-1/-2
Tensile Modulus  7.90 GPa 1150 ksi 50%RH; ISO 527-1/-2
  9.50 GPa 1380 ksi DAM; ISO 527-1/-2
  0.06617 GPa
@Temperature 220 °C		 9.597 ksi
@Temperature 428 °F		 DAM; Dynamic; ISO 11403-1 -2
  3.149 GPa
@Temperature 160 °C		 456.7 ksi
@Temperature 320 °F		 DAM; Dynamic; ISO 11403-1 -2
  5.282 GPa
@Temperature 80.0 °C		 766.1 ksi
@Temperature 176 °F		 DAM; Dynamic; ISO 11403-1 -2
  8.048 GPa
@Temperature 30.0 °C		 1167 ksi
@Temperature 86.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  8.123 GPa
@Temperature -20.0 °C		 1178 ksi
@Temperature -4.00 °F		 DAM; Dynamic; ISO 11403-1 -2
  8.15 GPa
@Temperature -50.0 °C		 1180 ksi
@Temperature -58.0 °F		 DAM; Dynamic; ISO 11403-1 -2
Flexural Modulus  7.00 GPa 1020 ksi 50%RH; ISO 178
  8.20 GPa 1190 ksi DAM; ISO 178
Shear Modulus   0.4945 GPa
@Temperature 160 °C		 71.72 ksi
@Temperature 320 °F		 DAM; Dynamic; ISO 11403-1 -2
  0.609 GPa
@Temperature 120 °C		 88.3 ksi
@Temperature 248 °F		 DAM; Dynamic; ISO 11403-1 -2
  0.861 GPa
@Temperature 70.0 °C		 125 ksi
@Temperature 158 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.649 GPa
@Temperature 20.0 °C		 239.2 ksi
@Temperature 68.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.729 GPa
@Temperature -20.0 °C		 250.8 ksi
@Temperature -4.00 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.806 GPa
@Temperature -50.0 °C		 261.9 ksi
@Temperature -58.0 °F		 DAM; Dynamic; ISO 11403-1 -2
Secant Modulus   1.97 GPa
@Strain 4.40 %,
Temperature 100 °C		 286 ksi
@Strain 4.40 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2.2438 GPa
@Strain 3.50 %,
Temperature 100 °C		 325.44 ksi
@Strain 3.50 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  2.40 GPa
@Strain 3.40 %,
Temperature 100 °C		 347 ksi
@Strain 3.40 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2.79 GPa
@Strain 3.00 %,
Temperature 80.0 °C		 405 ksi
@Strain 3.00 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2.80 GPa
@Strain 3.30 %,
Temperature 80.0 °C		 406 ksi
@Strain 3.30 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  2.88 GPa
@Strain 2.50 %,
Temperature 100 °C		 417 ksi
@Strain 2.50 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  3.17 GPa
@Strain 2.60 %,
Temperature 80.0 °C		 460 ksi
@Strain 2.60 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  3.31 GPa
@Strain 2.30 %,
Temperature 80.0 °C		 480 ksi
@Strain 2.30 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  3.31 GPa
@Strain 1.90 %,
Temperature 100 °C		 480 ksi
@Strain 1.90 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  3.43 GPa
@Strain 1.70 %,
Temperature 100 °C		 497 ksi
@Strain 1.70 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  3.47 GPa
@Strain 2.10 %,
Temperature 80.0 °C		 503 ksi
@Strain 2.10 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  4.01 GPa
@Strain 1.50 %,
Temperature 80.0 °C		 582 ksi
@Strain 1.50 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  4.02 GPa
@Strain 1.10 %,
Temperature 100 °C		 583 ksi
@Strain 1.10 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  4.12 GPa
@Strain 1.20 %,
Temperature 80.0 °C		 597 ksi
@Strain 1.20 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  4.3625 GPa
@Strain 3.20 %,
Temperature 23.0 °C		 632.74 ksi
@Strain 3.20 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4.548 GPa
@Strain 1.00 %,
Temperature 80.0 °C		 659.6 ksi
@Strain 1.00 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  4.70 GPa
@Strain 0.300 %,
Temperature 100 °C		 682 ksi
@Strain 0.300 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  4.86 GPa
@Strain 0.300 %,
Temperature 100 °C		 704 ksi
@Strain 0.300 %,
Temperature 212 °F		 50%RH; ISO 11403-1 -2
  4.99 GPa
@Strain 2.60 %,
Temperature 23.0 °C		 724 ksi
@Strain 2.60 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  5.00 GPa
@Strain 0.300 %,
Temperature 80.0 °C		 725 ksi
@Strain 0.300 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  5.31 GPa
@Strain 0.300 %,
Temperature 80.0 °C		 770 ksi
@Strain 0.300 %,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  6.62 GPa
@Strain 2.30 %,
Temperature 23.0 °C		 960 ksi
@Strain 2.30 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  6.67 GPa
@Strain 1.20 %,
Temperature 23.0 °C		 967 ksi
@Strain 1.20 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  6.68 GPa
@Strain 2.80 %,
Temperature 0.000 °C		 969 ksi
@Strain 2.80 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  6.76 GPa
@Strain 2.40 %,
Temperature 0.000 °C		 980 ksi
@Strain 2.40 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  6.76 GPa
@Strain 3.30 %,
Temperature -40.0 °C		 981 ksi
@Strain 3.30 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  7.31 GPa
@Strain 1.90 %,
Temperature 23.0 °C		 1060 ksi
@Strain 1.90 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  7.36 GPa
@Strain 0.500 %,
Temperature 23.0 °C		 1070 ksi
@Strain 0.500 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  7.44 GPa
@Strain 2.60 %,
Temperature -40.0 °C		 1080 ksi
@Strain 2.60 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  7.5068 GPa
@Strain 2.50 %,
Temperature -40.0 °C		 1088.8 ksi
@Strain 2.50 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  7.55 GPa
@Strain 2.20 %,
Temperature 0.000 °C		 1100 ksi
@Strain 2.20 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  7.91 GPa
@Strain 1.60 %,
Temperature 0.000 °C		 1150 ksi
@Strain 1.60 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  7.99 GPa
@Strain 1.50 %,
Temperature 23.0 °C		 1160 ksi
@Strain 1.50 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  8.20 GPa
@Strain 1.80 %,
Temperature -40.0 °C		 1190 ksi
@Strain 1.80 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  8.21 GPa
@Strain 1.90 %,
Temperature -40.0 °C		 1190 ksi
@Strain 1.90 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  8.61 GPa
@Strain 1.40 %,
Temperature 0.000 °C		 1250 ksi
@Strain 1.40 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  8.805 GPa
@Strain 1.00 %,
Temperature 23.0 °C		 1277 ksi
@Strain 1.00 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  8.86 GPa
@Strain 1.40 %,
Temperature -40.0 °C		 1280 ksi
@Strain 1.40 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  9.01 GPa
@Strain 0.900 %,
Temperature 0.000 °C		 1310 ksi
@Strain 0.900 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  9.13 GPa
@Strain 0.800 %,
Temperature 0.000 °C		 1320 ksi
@Strain 0.800 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  9.32 GPa
@Strain 0.600 %,
Temperature 23.0 °C		 1350 ksi
@Strain 0.600 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  9.32 GPa
@Strain 0.500 %,
Temperature 0.000 °C		 1350 ksi
@Strain 0.500 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  9.76 GPa
@Strain 0.700 %,
Temperature -40.0 °C		 1420 ksi
@Strain 0.700 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  9.84 GPa
@Strain 0.600 %,
Temperature -40.0 °C		 1430 ksi
@Strain 0.600 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Izod Impact, Notched (ISO)  12.0 kJ/m² 5.71 ft-lb/in² 50%RH; ISO 180/1A
  13.0 kJ/m² 6.19 ft-lb/in² DAM; ISO 180/1A
  10.0 kJ/m²
@Temperature -30.0 °C		 4.76 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
  10.0 kJ/m²
@Temperature -40.0 °C		 4.76 ft-lb/in²
@Temperature -40.0 °F		 50%RH; ISO 180/1A
  11.0 kJ/m²
@Temperature -40.0 °C		 5.23 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 180/1A
  11.0 kJ/m²
@Temperature -30.0 °C		 5.23 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
Izod Impact, Unnotched (ISO)  60.0 kJ/m² 28.6 ft-lb/in² 50%RH; ISO 180/1U
  70.0 kJ/m² 33.3 ft-lb/in² DAM; ISO 180/1U
  45.0 kJ/m²
@Temperature -30.0 °C		 21.4 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1U
  60.0 kJ/m²
@Temperature -30.0 °C		 28.6 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1U
Charpy Impact Unnotched  8.00 J/cm² 38.1 ft-lb/in² DAM; ISO 179/1eU
  9.00 J/cm² 42.8 ft-lb/in² 50%RH; ISO 179/1eU
  6.00 J/cm²
@Temperature -30.0 °C		 28.6 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
  6.50 J/cm²
@Temperature -30.0 °C		 30.9 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
Charpy Impact, Notched  1.20 J/cm² 5.71 ft-lb/in² 50%RH; ISO 179/1eA
  1.30 J/cm² 6.19 ft-lb/in² DAM; ISO 179/1eA
  1.00 J/cm²
@Temperature -30.0 °C		 4.76 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
  1.00 J/cm²
@Temperature -40.0 °C		 4.76 ft-lb/in²
@Temperature -40.0 °F		 50%RH; ISO 179/1eA
  1.10 J/cm²
@Temperature -30.0 °C		 5.23 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
  1.20 J/cm²
@Temperature -40.0 °C		 5.71 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+12 ohm-cm 1.00e+12 ohm-cm 50%RH; IEC 60093
  1.00e+15 ohm-cm 1.00e+15 ohm-cm DAM; IEC 60093
Surface Resistance  1.00e+12 ohm 1.00e+12 ohm 50%RH; IEC 60093
Dielectric Constant   3.8
@Frequency 1.00e+6 Hz		 3.8
@Frequency 1.00e+6 Hz		 DAM; IEC 60250
  4.1
@Frequency 100 Hz		 4.1
@Frequency 100 Hz		 DAM; IEC 60250
Dielectric Strength  30.0 kV/mm 762 kV/in 50%RH; IEC 60243-1
  33.0 kV/mm 838 kV/in DAM; IEC 60243-1
Dissipation Factor   0.0135
@Frequency 100 Hz		 0.0135
@Frequency 100 Hz		 DAM; IEC 60250
  0.015
@Frequency 1.00e+6 Hz		 0.015
@Frequency 1.00e+6 Hz		 DAM; IEC 60250
Comparative Tracking Index  600 V 600 V DAM; IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  17.0 µm/m-°C 9.44 µin/in-°F DAM; ISO 11359-1/-2
  16.0 µm/m-°C
@Temperature 55.0 - 160 °C		 8.89 µin/in-°F
@Temperature 131 - 320 °F		 DAM; ISO 11359-1/-2
  26.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		 14.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		 DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  113 µm/m-°C 62.8 µin/in-°F DAM; ISO 11359-1/-2
  83.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		 46.1 µin/in-°F
@Temperature -40.0 - 73.4 °F		 DAM; ISO 11359-1/-2
  158 µm/m-°C
@Temperature 55.0 - 160 °C		 87.8 µin/in-°F
@Temperature 131 - 320 °F		 DAM; ISO 11359-1/-2
Specific Heat Capacity  2.13 J/g-°C 0.509 BTU/lb-°F  
Thermal Conductivity  0.260 W/m-K 1.80 BTU-in/hr-ft²-°F of melt
Melting Point  218 °C 424 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  216 °C 421 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  200 °C 392 °F DAM; ISO 75-1/-2
Glass Transition Temp, Tg  65.0 °C 149 °F DAM; 10°C/min; ISO 11357-1/-2
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; IEC 60695-11-10
  HB
@Thickness 0.700 mm		 HB
@Thickness 0.0276 in		 DAM; IEC 60695-11-10
Flame Spread  23 mm/min
@Thickness 1.00 mm		 0.91 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
Oxygen Index  23 % 23 % DAM; ISO 4589-1/-2
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Eff. thermal diffusivity 7.50E-08 m²/s  
Part Marking Code >PA612-GF33< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PA612-GF33  
  PA612-GF33 ISO 1043
UL recognition UL DAM

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39823.html

免责声明: 本文 PA612 美国杜邦77G33L NC010矿物增强 注塑级 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4