| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 4.9 % @Thickness 2.00 mm |
4.9 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Moisture Absorption | 1.50 % @Thickness 2.00 mm |
1.50 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Viscosity Test | 137 cm³/g | 137 cm³/g | DAM; ISO 307 1157 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | DAM; ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | DAM; ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 169 MPa | 24500 psi | DAM; ISO 527-1/-2 | ||
| Tensile Stress | 8.6609 MPa @Strain 0.200 %, Temperature 150 °C |
1256.2 psi @Strain 0.200 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | ||
| 12.0 MPa @Strain 0.100 %, Temperature 23.0 °C |
1740 psi @Strain 0.100 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 12.2 MPa @Strain 0.100 %, Temperature -40.0 °C |
1770 psi @Strain 0.100 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 18.66 MPa @Strain 0.500 %, Temperature 150 °C |
2706 psi @Strain 0.500 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |||
| 25.98 MPa @Strain 0.800 %, Temperature 150 °C |
3768 psi @Strain 0.800 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |||
| 38.83 MPa @Strain 1.60 %, Temperature 150 °C |
5632 psi @Strain 1.60 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |||
| 61.66 MPa @Strain 7.00 %, Temperature 150 °C |
8943 psi @Strain 7.00 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |||
| 66.96 MPa @Strain 0.600 %, Temperature 23.0 °C |
9712 psi @Strain 0.600 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 78.69 MPa @Strain 0.700 %, Temperature -40.0 °C |
11410 psi @Strain 0.700 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 93.42 MPa @Strain 0.900 %, Temperature 23.0 °C |
13550 psi @Strain 0.900 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 114.9 MPa @Strain 1.20 %, Temperature 23.0 °C |
16660 psi @Strain 1.20 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 125.4 MPa @Strain 1.20 %, Temperature -40.0 °C |
18180 psi @Strain 1.20 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 156.6 MPa @Strain 1.60 %, Temperature -40.0 °C |
22710 psi @Strain 1.60 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 227.4 MPa @Strain 3.10 %, Temperature -40.0 °C |
32980 psi @Strain 3.10 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| Elongation at Break | 3.3 % | 3.3 % | DAM; ISO 527-1/-2 | ||
| Tensile Modulus | 11.7 GPa | 1700 ksi | DAM; ISO 527-1/-2 | ||
| Flexural Modulus | 10.3 GPa | 1490 ksi | DAM; ISO 178 | ||
| Secant Modulus | 2.59 GPa @Strain 2.90 %, Temperature 100 °C |
376 ksi @Strain 2.90 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | ||
| 3.63 GPa @Strain 1.50 %, Temperature 100 °C |
527 ksi @Strain 1.50 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 4.53 GPa @Strain 0.800 %, Temperature 100 °C |
658 ksi @Strain 0.800 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 5.30 GPa @Strain 0.400 %, Temperature 100 °C |
769 ksi @Strain 0.400 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 5.90 GPa @Strain 0.100 %, Temperature 100 °C |
856 ksi @Strain 0.100 %, Temperature 212 °F |
DAM; ISO 11403-1 -2 | |||
| 7.51 GPa @Strain 2.00 %, Temperature 23.0 °C |
1090 ksi @Strain 2.00 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 8.12 GPa @Strain 2.60 %, Temperature -40.0 °C |
1180 ksi @Strain 2.60 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 9.04 GPa @Strain 1.40 %, Temperature 23.0 °C |
1310 ksi @Strain 1.40 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 9.11 GPa @Strain 2.00 %, Temperature -40.0 °C |
1320 ksi @Strain 2.00 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 10.103 GPa @Strain 1.00 %, Temperature 23.0 °C |
1465.3 ksi @Strain 1.00 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 10.3 GPa @Strain 1.30 %, Temperature -40.0 °C |
1490 ksi @Strain 1.30 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 11.2 GPa @Strain 0.600 %, Temperature 23.0 °C |
1620 ksi @Strain 0.600 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 11.2 GPa @Strain 0.700 %, Temperature -40.0 °C |
1630 ksi @Strain 0.700 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| 12.0 GPa @Strain 0.100 %, Temperature 23.0 °C |
1740 ksi @Strain 0.100 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |||
| 12.2 GPa @Strain 0.100 %, Temperature -40.0 °C |
1770 ksi @Strain 0.100 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |||
| Izod Impact, Notched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | DAM; ISO 180/1A | ||
| 14.0 kJ/m² @Temperature -40.0 °C |
6.66 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 78.0 kJ/m² | 37.1 ft-lb/in² | DAM; ISO 180/1U | ||
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 2.30 J/cm² | 10.9 ft-lb/in² | DAM; ISO 179/1eA | ||
| 1.50 J/cm² @Temperature -40.0 °C |
7.14 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 262 °C | 504 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 261 °C | 502 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | DAM; ISO 75-1/-2 | ||
| Vicat Softening Point | 215 °C | 419 °F | DAM; 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | ||
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
DAM; IEC 60695-11-10 | |||
| Oxygen Index | 27 % | 27 % | DAM; ISO 4589-1/-2 | ||
| De |
|||||
| Additives | Lubricants | ||||
| Release agent | |||||
| Delivery form | Pellets | ||||
| Part Marking Code | >PA66-IGF43< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA66-IGF43 | ||||
| Special characteristics | Heat stabilised or stable to heat | ||||
概述
PA塑料(尼龙，聚酰胺)，英文名称:Polyamide
PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型温度：220-300℃
干燥条件：100-110℃/12小时
坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味
|
尼龙6： |
弹性好，冲击强度，吸水较大 |
|
尼龙66： |
性能优于尼龙6，强度高，耐磨性好 |
|
尼龙610： |
与尼龙66相似，但吸水小，刚度低 |
|
尼龙1010： |
半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件 |
成型性能
1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。
2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。
3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。
4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。
5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。
聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。
应用
汽车制造方面
用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。
电器电子工业
可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。
医疗器械仪器
用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。
其它方面
用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。