LCP S625 材质说明：低摩擦耐磨性。
LCP S625 形式：粒子
LCP S625 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.000 cm/cm | 0.000 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00800 cm/cm | 0.00800 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 121 MPa | 17500 psi | 50mm/min; ISO 527-2/1A |
| Elongation at Break | 3.00 % | 3.00 % | 50mm/min; ISO 527-2/1A |
| Tensile Modulus | 8.30 GPa | 1200 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 152 MPa | 22000 psi | ISO 178 |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO 180/1A |
| 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 350 °C | 662 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 271 °C | 520 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 129 °C | 264 °F | ISO 75-1, -2 |
| Vicat Softening Point | 227 °C | 441 °F | |