| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.71 g/cc | 0.0618 lb/in³ | |
| Water Absorption | 0.00 % | 0.00 % | |
| Moisture Absorption at Equilibrium | <= 0.50 % | <= 0.50 % | Humidity Absorption |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 160 MPa | 23200 psi | |
| Elongation at Break | 1.0 % | 1.0 % | |
| Modulus of Elasticity | 15.0 GPa | 2180 ksi | |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | |
| 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | |
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
||
| Tensile Impact Strength | 80.0 kJ/m² | 38.1 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 15000 MPa | 2.18e+6 psi | |
| Tensile Creep Modulus, 1000 hours | 10000 MPa | 1.45e+6 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
|
| 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | |
| Dissipation Factor | 0.0040 @Frequency 100 Hz |
0.0040 @Frequency 100 Hz |
|
| 0.015 @Frequency 1e+6 Hz |
0.015 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 500 V | 500 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | |
| Vicat Softening Point | 215 °C | 419 °F | 50°C/hr/50 N |
| UL RTI, Electrical | 130 °C | 266 °F | |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | |
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||