| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.850 g/cc | 0.0307 lb/in³ | |
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Water Absorption | 0.80 % | 0.80 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH; ISO 62 |
| Melt Flow | 1.112 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.112 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 130 MPa @Load 36.5 kg, Time 30.0 sec |
18900 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527-2 |
| Elongation at Break | 25 % | 25 % | 50mm/min; ISO 527-2 |
| Elongation at Yield | 9.0 % | 9.0 % | ISO 527-2 |
| Modulus of Elasticity | 2.45 GPa | 355 ksi | ISO 527-2 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 20.0 J/cm² @Temperature -30.0 °C |
95.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 23.0 J/cm² @Temperature 23.0 °C |
109 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1000 hours | 1050 MPa @Strain <=0.500 % |
152000 psi @Strain <=0.500 % |
ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 |
| 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0010 @Frequency 100 Hz |
0.0010 @Frequency 100 Hz |
IEC 60250 |
| 0.0050 @Frequency 1.00e+6 Hz |
0.0050 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Test solution B; IEC 60112 |
| 600 V | 600 V | Test solution A; IEC 60112 | |