| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.750 % @Thickness 2.00 mm |
0.750 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Moisture Absorption | 0.150 % @Thickness 2.00 mm |
0.150 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00200 cm/cm | 0.00200 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.00800 cm/cm | 0.00800 in/in | ISO 294-4, 2577 | ||
| Melt Flow | 6.00 g/10 min @Load 2.16 kg, Temperature 280 °C |
6.00 g/10 min @Load 4.76 lb, Temperature 536 °F |
cm³/10 min volumetric rate; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.00 % | 2.00 % | ISO 527-1/-2 | ||
| Tensile Modulus | 11.5 GPa | 1670 ksi | ISO 527-1/-2 | ||
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | ||
| 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 11200 MPa | 1.62e+6 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 9700 MPa | 1.41e+6 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 4.70 @Frequency 1.00e+6 Hz |
4.70 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 4.80 @Frequency 100 Hz |
4.80 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00700 @Frequency 100 Hz |
0.00700 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0100 @Frequency 1.00e+6 Hz |
0.0100 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 | ||
| 250 - 400 V @Temperature 23.0 °C |
250 - 400 V @Temperature 73.4 °F |
UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C | 10.6 µin/in-°F | ISO 11359-1/-2 | ||
| 22.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
12.2 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 92.0 µm/m-°C | 51.1 µin/in-°F | ISO 11359-1/-2 | ||
| 68.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |||
| Melting Point | 252 °C | 486 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 220 °C | 428 °F | 50°C/h, 50N; ISO 306 | ||
| UL RTI, Electrical | 155 °C @Thickness 0.400 mm |
311 °F @Thickness 0.0157 in |
UL 746B | ||
| 155 °C @Thickness 0.750 mm |
311 °F @Thickness 0.0295 in |
UL 746B | |||
| 155 °C @Thickness 1.50 mm |
311 °F @Thickness 0.0591 in |
UL 746B | |||
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
IEC 60695-11-10 | ||
| V-0 @Thickness 0.350 mm |
V-0 @Thickness 0.0138 in |
IEC 60695-11-10 | |||
| 5VA @Thickness 1.50 mm |
5VA @Thickness 0.0591 in |
IEC 60695-11-20 | |||
| Oxygen Index | 33.0 % | 33.0 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | >= 270 °C | >= 518 °F | |||
| 280 °C | 536 °F | Optimum | |||
| <= 290 °C | <= 554 °F | ||||
| Mold Temperature | >= 100 °C | >= 212 °F | |||
| 110 °C | 230 °F | Optimum | |||
| <= 120 °C | <= 248 °F | ||||
| Ejection Temperature | 170 °C | 338 °F | |||
| Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
|||
| Moisture Content | 0.0200 % | 0.0200 % | |||
| Hold Pressure | 80.0 MPa | 11600 psi | |||
| De |
|||||
| Additive | Release agent | ||||
| Back pressure | As low as possible | ||||
| Delivery form | Pellets | ||||
| Drying Recommended | yes | ||||
| Eff. thermal diffusivity (m²/s) | 1.10E-07 | ||||
| Hold pressure time | 4 s/mm | ||||
| Max. screw tangential speed (m/s) | 0.2 | ||||
| Part Marking Code | >PET-GF30FR(17)< | ISO 11469 | |||
| Processing | Injection Molding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PET-GF30FR(17) | ISO 1043 |
|||