| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | Crystalline; ISO 1183 | ||
| Water Absorption at Saturation | 0.50 % @Temperature 23.0 °C |
0.50 % @Temperature 73.4 °F |
Equilibrium; by immersion; ISO 62-1 | ||
| 0.60 % @Temperature 100 °C |
0.60 % @Temperature 212 °F |
immersion; ISO 62-1 | |||
| Viscosity | 525000 cP @Temperature 400 °C |
525000 cP @Temperature 752 °F |
melt; ISO 11443 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | 360°C nozzle, 160°C tool; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | 405°C nozzle, 200°C tool; ISO 294-4 | ||
| Spiral Flow | 8.00 cm @Thickness 1.00 mm |
3.15 in @Thickness 0.0394 in |
405°C nozzle, 200°C tool | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 88 | 88 | ISO 868 | ||
| Tensile Strength at Break | 70.0 MPa @Temperature 275 °C |
10200 psi @Temperature 527 °F |
ISO 527 | ||
| 80.0 MPa @Temperature 225 °C |
11600 psi @Temperature 437 °F |
ISO 527 | |||
| 110 MPa @Temperature 175 °C |
16000 psi @Temperature 347 °F |
ISO 527 | |||
| 170 MPa @Temperature 125 °C |
24700 psi @Temperature 257 °F |
ISO 527 | |||
| 275 MPa @Temperature 23.0 °C |
39900 psi @Temperature 73.4 °F |
ISO 527 | |||
| Elongation at Break | 1.7 % @Temperature 23.0 °C |
1.7 % @Temperature 73.4 °F |
ISO 527 | ||
| Tensile Modulus | 28.0 GPa @Temperature 23.0 °C |
4060 ksi @Temperature 73.4 °F |
ISO 527 | ||
| Flexural Strength | 100 MPa @Temperature 275 °C |
14500 psi @Temperature 527 °F |
ISO 178 | ||
| 185 MPa @Temperature 175 °C |
26800 psi @Temperature 347 °F |
ISO 178 | |||
| 265 MPa @Temperature 125 °C |
38400 psi @Temperature 257 °F |
ISO 178 | |||
| 400 MPa @Temperature 23.0 °C |
58000 psi @Temperature 73.4 °F |
ISO 178 | |||
| Flexural Modulus | 23.5 GPa @Temperature 23.0 °C |
3410 ksi @Temperature 73.4 °F |
ISO 178 | ||
| Compressive Strength | 65.0 MPa @Temperature 250 °C |
9430 psi @Temperature 482 °F |
ISO 604 | ||
| 95.0 MPa @Temperature 200 °C |
13800 psi @Temperature 392 °F |
ISO 604 | |||
| 210 MPa @Temperature 120 °C |
30500 psi @Temperature 248 °F |
ISO 604 | |||
| 300 MPa @Temperature 23.0 °C |
43500 psi @Temperature 73.4 °F |
ISO 604 | |||
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | ||
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180/U | ||
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1U | ||
| Charpy Impact, Notched | 0.650 J/cm² @Temperature 23.0 °C |
3.09 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1e+05 | 1e+05 | 1V; ASTM D4496 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 35.0 µm/m-°C @Temperature <=152 °C |
19.4 µin/in-°F @Temperature <=306 °F |
Average below Tg; ISO 11359 | ||
| 90.0 µm/m-°C @Temperature >=152 °C |
50.0 µin/in-°F @Temperature >=306 °F |
Average above Tg; ISO 11359 | |||
| CTE, linear, Parallel to Flow | 5.00 µm/m-°C @Temperature >=152 °C |
2.78 µin/in-°F @Temperature >=306 °F |
Above Tg; ISO 11359 | ||
| 5.00 µm/m-°C @Temperature <=152 °C |
2.78 µin/in-°F @Temperature <=306 °F |
Below Tg; ISO 11359 | |||
| Thermal Conductivity | 2.00 W/m-K | 13.9 BTU-in/hr-ft²-°F | Along flow; ISO 22007-4 | ||
| 0.950 W/m-K @Temperature 23.0 °C |
6.59 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
Average; ISO/CD 22007-4 | |||
| Melting Point | 373 °C | 703 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 368 °C | 694 °F | ISO 75-f | ||
| Glass Transition Temp, Tg | 152 °C | 306 °F | Onset; ISO 11357 | ||
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature | ||
| Nozzle Temperature | 405 °C | 761 °F | |||
| Mold Temperature | 190 - 215 °C | 374 - 419 °F | |||
| Drying Temperature | 120 °C @Time 18000 sec |
248 °F @Time 5.00 hour |
|||
| 150 °C @Time 10800 sec |
302 °F @Time 3.00 hour |
||||
| De |
|||||
| Toxicity Index | 0.05 | NES 713; CO content | |||
| 0.12 | NES 713; CO2 content | ||||
| 0.17 | NES 713; Total gases |
||||
.