拜耳 FR3001 PC/ABS共混物

拜耳 FR3001 PC/ABS共混物 类别:聚合物;热塑性的;聚合物;聚碳酸酯/ ABS合金,无筋;聚碳酸酯(PC) 材料说明:(PC+ABS)混合;维卡/ B 120温度为103 C°UL 94 V-0;识别1.5毫米;灼热丝温度(易燃指数):960°C在2毫米
物性表:
 
Physical Properties Metric English Comments
Density  1.18 g/cc 0.0426 lb/in³ ISO 1183-1
Moisture Absorption at Equilibrium  0.20 % 0.20 % ISO 62, 50% RH
Water Absorption at Saturation  0.50 % 0.50 % ISO 62
Viscosity  150000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C
150000 cP
@Shear Rate 1000 1/s,
Temperature 500 °F
melt viscosity; b.o. ISO 11443-A
Linear Mold Shrinkage, Flow  0.0050 - 0.0070 cm/cm
@Thickness 3.00 mm
0.0050 - 0.0070 in/in
@Thickness 0.118 in
150x105x3mm; b.o. ISO 2577
Linear Mold Shrinkage, Transverse  0.0050 - 0.0070 cm/cm
@Thickness 3.00 mm
0.0050 - 0.0070 in/in
@Thickness 0.118 in
150x105x3mm; b.o. ISO 2577
Melt Flow  29.5 g/10 min
@Load 0.510 kg,
Temperature 240 °C
29.5 g/10 min
@Load 1.12 lb,
Temperature 464 °F
ISO 1133
Spiral Flow  48.0 cm 18.9 in 260 °C/80°C; 2 x 8 mm; Bayer test
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  50.0 MPa 7250 psi 50 mm/min; ISO 527-1,-2
Tensile Strength, Yield  60.0 MPa 8700 psi 50 mm/min; ISO 527-1,-2
Elongation at Break  >= 30 % >= 30 % 50 mm/min; b.o. ISO 527-1,-2
Elongation at Yield  4.0 % 4.0 % 50 mm/min; ISO 527-1,-2
Tensile Modulus  2.70 GPa 392 ksi 1 mm/min; ISO 527-1,-2
Izod Impact, Notched (ISO)   8.00 kJ/m²
@Temperature -30.0 °C
3.81 ft-lb/in²
@Temperature -22.0 °F
ISO 180-A
  15.0 kJ/m²
@Temperature 23.0 °C
7.14 ft-lb/in²
@Temperature 73.4 °F
ISO 180-A
Izod Impact, Unnotched (ISO)  NB
@Temperature 23.0 °C
NB
@Temperature 73.4 °F
ISO 180-U
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+14 ohm-cm 1.00e+14 ohm-cm IEC 60093
Surface Resistance  1.00e+16 ohm 1.00e+16 ohm IEC 60093
Dielectric Constant   3.1
@Frequency 1.00e+6 Hz
3.1
@Frequency 1.00e+6 Hz
IEC 60250
  3.2
@Frequency 100 Hz
3.2
@Frequency 100 Hz
IEC 60250
Dielectric Strength  30.0 kV/mm
@Thickness 1.00 mm
762 kV/in
@Thickness 0.0394 in
IEC 60243-1
Dissipation Factor   0.0050
@Frequency 100 Hz
0.0050
@Frequency 100 Hz
IEC 60250
  0.0070
@Frequency 1.00e+6 Hz
0.0070
@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index  300 V 300 V Solution A; IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  76.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
42.2 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1,-2
CTE, linear, Transverse to Flow  80.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
44.4 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1,-2
Deflection Temperature at 0.46 MPa (66 psi)  98.0 °C 208 °F ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi)  88.0 °C 190 °F ISO 75-1,-2
Vicat Softening Point  103 °C
@Load 5.10 kg
217 °F
@Load 11.2 lb
120°C/h; ISO 306
Flammability, UL94   V-0
@Thickness 1.50 mm
V-0
@Thickness 0.0591 in
 
  5VB
@Thickness 2.00 mm
5VB
@Thickness 0.0787 in
 
  5VA
@Thickness 3.00 mm
5VA
@Thickness 0.118 in
 
 
Processing Properties Metric English Comments
Melt Temperature  240 °C 464 °F Injection molding; ISO 294
Mold Temperature  80.0 °C 176 °F Injection molding; ISO 294
Injection Velocity  240 mm/sec 9.45 in/sec ISO 294
 

图:


上海松翰塑化科技有限公司!本公司承诺,假一赔百!所有产品都是原厂家,原包装一线独家营销!
我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
欢迎新老客户来电或QQ咨询:
联系人:李生
联系电话;13636696005
联系QQ;1020580970
联系邮箱;1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-41573.html

免责声明: 本文 拜耳 FR3001 PC/ABS共混物 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4