Availability
|
|
|
Filler / Reinforcement
|
|
|
Features
|
|
|
Forms
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.46
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage - Flow
|
0.35
|
%
|
ISO 294-4 |
|
Water Absorption
|
ISO 62 | ||
|
Saturation, 23°C
|
4.4
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
1.4
|
%
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
7600
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Break, 23°C)
|
85.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break, 23°C)
|
1.5
|
%
|
ISO 527-2 |
|
Flexural Modulus (23°C)
|
7200
|
MPa
|
ISO 178 |
|
Flexural Strength (23°C)
|
115
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (23°C)
|
4.0
|
kJ/m²
|
ISO 179 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
|||
|
0.45 MPa, Unannealed
|
245
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
235
|
°C
|
ISO 75-2/A |
|
CLTE - Flow (23°C)
|
0.000029
|
cm/cm/°C
|
ISO 11359-2 |
|
Thermal Conductivity
|
2.1
|
W/m/K
|
ISO 8302 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+12
|
ohm
|
ASTM D257 |
|
Electric Strength (2.00 mm)
|
37
|
kV/mm
|
IEC 60243-1 |
|
Comparative Tracking Index
|
600
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating (1.60 mm)
|
HB
|
|
UL 94 |
| Additional Information | |||
|
The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods.
The value listed as Coefficient of Linear Thermal Expansion, Flow ISO 11359-1-2, was tested in accordance with ISO 7991. |