流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔体体积流动速率(Melt volume-flow rate) (MVR)	8	cm³/10min	ISO 1133
温度(Temperature)	220	°C	ISO 1133
负载(Load)	2.16	kg	ISO 1133
成型收缩(Molding shrinkage) (parallel)	1.4	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	1.4	%	ISO 294-4, 2577

[tr][/tr][tr][/tr]

机械性能(机械性能(Mechanical properties))

值(Value)

单位(Unit)

测试标准(Test Standard)

ISO数据(ISO数据(CAMPUS/ISO) Data)

拉伸模量(Tensile Modulus)

180

MPa

ISO 527-1/-2

屈服应力(Yield stress)

MPa

ISO 527-1/-2

屈服应变(Yield strain)

ISO 527-1/-2

断裂拉伸应变(Nominal strain at break)

>50

ISO 527-1/-2

Tensile creep modulus (1h)

170

MPa

ISO 899-1

Tensile creep modulus (1000h)

130

MPa

ISO 899-1

简支梁冲击强度(Charpy impact strength) (+23°C)

kJ/m²

ISO 179/1eU

简支梁冲击强度(Charpy impact strength) (-30°C)

kJ/m²

ISO 179/1eU

简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)

kJ/m²

ISO 179/1eA

简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)

150[P]

kJ/m²

ISO 179/1eA

Tensile notched impact strength (+23°C)

300

kJ/m²

ISO 8256/1

Stress at 10% elongation

MPa

ISO 527-1/-2

Stress at 100% elongation

MPa

ISO 527-1/-2

破坏时应变(Strain at break) TPE

>300

ISO 527-1/-2

破坏时应变(Stress at break) TPE

MPa

ISO 527-1/-2

抗拉强度(撕裂强度(Tear strength))

137

kN/m

ISO 34-1

Abrasion resistance

120

mm³

ISO 4649

Shore D hardness (15s)

ISO 868

Partial Break

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	202	°C	ISO 11357-1/-3
玻璃化转变温度(Glass transition temperature) (10°C/min)	-20	°C	ISO 11357-1/-2
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	45	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	70	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	75	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	180	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	180	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.5	mm	IEC 60695-11-10
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	3.0	mm	IEC 60695-11-10
Oxygen index	20	%	ISO 4589-1/-2

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (100Hz)	4.8	-	IEC 60250
相对介电常数(Relative permittivity) (1MHz)	4.4	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (100Hz)	90	E-4	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	375	E-4	IEC 60250
体积电阻率(Volume resistivity)	4E11	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	>1E15	Ohm	IEC 60093
电气强度(Electric strength)	19	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	600	-	IEC 60112

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	0.6	%	Sim. to ISO 62
吸湿性(Humidity absorption)	0.2	%	Sim. to ISO 62
密度(Density)	1190	kg/m³	ISO 1183

流变计算属性(Rheological calculation properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density) of melt	1030	kg/m³	-
Eff. thermal diffusivity	5.44E-8	m²/s	-

Diagrams ISO 1817 Liquid C) (23°C)

ISO 1817 Liquid 4) (23°C)

ISO 1817 Liquid F) (23°C)

ISO 1817 Liquid F) (90°C)

ISO 1817 Liquid F) (>90°C)

Salt solutions

4 Brake fluid (130°C)