HDPE/DGDC-2100 NT 7/美国陶氏
- 生产企业： 美国陶氏
①原料描述部分
| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | 挤压，吹薄用 | ||
| 备注说明 | |||
②加工条件
| 加工条件 |
|---|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-792 | 0.950 | g/cm3 | ||
| 熔体流动速率 | 190℃/21.6kg | ASTM D-1238 | 9.0 | g/10min | ||
| 薄膜厚度 | 0.500 | mil | ||||
| 熔点 | DSC | 128 | ℃ | |||
| 机械性能 | 切割模量 | MD | ASTM D-882 | 965.2 | MPa | |
| TD | ASTM D-882 | 1096.2 | MPa | |||
| 屈服拉伸强度 | MD | ASTM D-882 | 42.3 | MPa | ||
| TD | ASTM D-882 | 31.7 | MPa | |||
| 断裂拉伸强度 | MD | ASTM D-882 | 93.7 | MPa | ||
| TD | ASTM D-882 | 68.8 | MPa | |||
| 断裂伸长率 | MD | ASTM D-882 | 330 | % | ||
| TD | ASTM D-882 | 410 | % | |||
| 缺口冲击强度 | ASTM D-1709 | 350 | g | |||
| 埃尔曼多夫撕裂强度 | MD | ASTM D-1922 | 11 | g | ||
| TD | ASTM D-1922 | 73 | g | |||
| 光学性能 | 光泽度 | ASTM D-2457 | 9 | |||
| 雾度 | ASTM D-1003 | 69 | % | |||