Availability
|
|
|
Filler / Reinforcement
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.48 to 1.50
|
g/cm³
|
ASTM D792 |
|
Molding Shrinkage - Flow
|
0.80 to 1.2
|
%
|
ASTM D955 |
|
Water Absorption (24 hr)
|
0.60
|
%
|
ASTM D570 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness
|
ASTM D785 | ||
|
M-Scale
|
95
|
|
|
|
R-Scale
|
122
|
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength
|
89.6
|
MPa
|
ASTM D638 |
|
Tensile Elongation (Break)
|
10 to 15
|
%
|
ASTM D638 |
|
Flexural Modulus
|
6210
|
MPa
|
ASTM D790 |
|
Flexural Strength
|
138
|
MPa
|
ASTM D790 |
|
Compressive Strength
|
252
|
MPa
|
ASTM D695 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (23°C, 3.18 mm)
|
37
|
J/m
|
ASTM D256 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
ASTM D648 | ||
|
0.45 MPa, Unannealed
|
210
|
°C
|
|
|
1.8 MPa, Unannealed
|
171
|
°C
|
|
|
Melting Temperature
|
254 to 266
|
°C
|
| Flammability |
Nominal Value
|
|
Test Method
|
|
Flame Rating
|
HB
|
|
UL 94 |