Availability
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
|||
|
Appearance
|
|
|||
|
Resin ID (ISO 1043)
|
|
| Physical | Dry | Conditioned |
Unit
|
Test Method
|
|
Density (23°C)
|
1.10
|
--
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage
|
ISO 294-4 | |||
|
Across Flow
|
2.2
|
--
|
%
|
|
|
Flow
|
2.1
|
--
|
%
|
|
|
Humidity Absorption - 62% RH (70°C)
|
2.1
|
--
|
%
|
ISO 1110 |
| Hardness | Dry | Conditioned |
Unit
|
Test Method
|
|
Shore Hardness (Shore D, 23°C)
|
75
|
--
|
|
DIN 53505 |
| Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
|
Tensile Modulus
|
2700
|
1300
|
MPa
|
ISO 527-2/1 |
|
Tensile Stress (Yield)
|
63.0
|
45.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Strain (Break)
|
> 35
|
> 100
|
%
|
ISO 527-2/50 |
|
Flexural Modulus 2
|
2500
|
--
|
MPa
|
ISO 178 |
|
Flexural Strength 2
|
90.0
|
--
|
MPa
|
ISO 178 |
|
Flexural Strain at Break 2
|
7.5
|
--
|
%
|
ISO 178 |
| Impact | Dry | Conditioned |
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-30°C
|
10
|
--
|
kJ/m²
|
|
|
23°C
|
15
|
25
|
kJ/m²
|
|
|
Charpy Unnotched Impact Strength (23°C)
|
No Break
|
No Break
|
|
ISO 179/1eU |
|
Notched Izod Impact Strength
|
ISO 180/1A | |||
|
-40°C
|
12
|
--
|
kJ/m²
|
|
|
-20°C
|
12
|
--
|
kJ/m²
|
|
|
23°C
|
15
|
--
|
kJ/m²
|
| Thermal | Dry | Conditioned |
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
213
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
70.0
|
--
|
°C
|
ISO 75-2/A |
|
Melting Temperature 3
|
262
|
--
|
°C
|
DIN EN 11357-1 |
| Electrical | Dry | Conditioned |
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+14
|
--
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
1.0E+15
|
--
|
ohm·cm
|
IEC 60093 |
|
Comparative Tracking Index (Solution A)
|
600
|
--
|
V
|
IEC 60112 |
| Flammability | Dry | Conditioned |
Unit
|
Test Method
|
|
Burning Rate 4 (1.00 mm)
|
< 100
|
--
|
mm/min
|
FMVSS 302 |
|
Flame Rating (1.60 mm)
|
HB
|
--
|
|
UL 94 |