Availability
|
|
|
Filler / Reinforcement
|
|
|
RoHS Compliance
|
|
|
Forms
|
|
| Physical | Dry | Conditioned |
Unit
|
Test Method
|
|
Density
|
1.25
|
--
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage
|
ISO 294-4 | |||
|
Across Flow
|
1.5
|
--
|
%
|
|
|
Flow
|
1.0
|
--
|
%
|
|
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
8.0
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
2.1
|
--
|
%
|
| Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
|
Tensile Modulus
|
5800
|
3000
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Break)
|
105
|
72.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break)
|
4.0
|
9.0
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
4700
|
--
|
MPa
|
ISO 178 |
|
Flexural Strength
|
165
|
--
|
MPa
|
ISO 178 |
| Impact | Dry | Conditioned |
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-30°C
|
3.0
|
3.0
|
kJ/m²
|
|
|
23°C
|
4.0
|
6.0
|
kJ/m²
|
| Thermal | Dry | Conditioned |
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
250
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
240
|
--
|
°C
|
ISO 75-2/A |
|
Melting Temperature 2
|
260
|
--
|
°C
|
ISO 11357-3 |
| Flammability | Dry | Conditioned |
|
Test Method
|
|
Flammability Classification
|
IEC 60695-11-10, -20 | |||
|
0.710 mm
|
HB
|
--
|
|
|
|
1.50 mm
|
HB
|
--
|