Availability
|
|
|
Filler / Reinforcement
|
|
|
Additive
|
|
|
Features
|
|
|
Forms
|
|
| Physical | Dry | Conditioned |
Unit
|
Test Method
|
|
Density
|
1.34
|
--
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage - Flow
|
0.45
|
--
|
%
|
ISO 294-4 |
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
4.5
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
0.70
|
--
|
%
|
| Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
6900
|
5100
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Break, 23°C)
|
160
|
110
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break, 23°C)
|
3.0
|
5.0
|
%
|
ISO 527-2 |
|
Flexural Modulus (23°C)
|
6500
|
4800
|
MPa
|
ISO 178 |
|
Flexural Strength (23°C)
|
190
|
150
|
MPa
|
ISO 178 |
| Impact | Dry | Conditioned |
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (23°C)
|
13
|
--
|
kJ/m²
|
ISO 179 |
|
Charpy Unnotched Impact Strength (23°C)
|
90
|
--
|
kJ/m²
|
ISO 179 |
| Thermal | Dry | Conditioned |
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
250
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
245
|
--
|
°C
|
ISO 75-2/A |
|
CLTE - Flow (23°C)
|
0.000030
|
--
|
cm/cm/°C
|
ISO 11359-2 |
|
Thermal Conductivity
|
0.28
|
--
|
W/m/K
|
ISO 8302 |
| Electrical | Dry | Conditioned |
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+12
|
--
|
ohm
|
ASTM D257 |
|
Electric Strength (2.00 mm)
|
35
|
30
|
kV/mm
|
IEC 60243-1 |
|
Comparative Tracking Index
|
500
|
500
|
V
|
IEC 60112 |
| Flammability | Dry | Conditioned |
Unit
|
Test Method
|
|
Flame Rating (1.60 mm)
|
HB
|
--
|
|
UL 94 |
| Additional Information | ||||
|
Dry
|
The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods.
The value listed as Coefficient of Linear Thermal Expansion, Flow ISO 11359-1-2, was tested in accordance with ISO 7991. |
|||