- 密度 [g/cm3]: 0.95
- 拉伸强度 [MPa]: 2.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D1505 | ||
| Vinyl Acetate Content | 23.5 - 26.5 % | 23.5 - 26.5 % | Arkema | ||
| Melt Index of Compound | 5.5 - 9.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.5 - 9.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 82 | 82 | ASTM D2240 | ||
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 | ||
| 26.0 MPa | 3770 psi | Film Property, 50 µm thickness; ASTM D882 | |||
| Tensile Strength, Yield | 2.60 MPa | 377 psi | ASTM D638 | ||
| 4.00 MPa | 580 psi | Film Property, 50 µm thickness; ASTM D882 | |||
| Elongation at Break | 600 - 900 % | 600 - 900 % | ASTM D638 | ||
| 700 - 900 % | 700 - 900 % | Film Property, 50 µm thickness; ASTM D882 | |||
| Dart drop Test | 400 g | 0.882 lb | ASTM D1709 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 80.0 °C | 176 °F | DSC | ||
| Vicat Softening Point | 49.0 °C | 120 °F | ASTM D1525 | ||
| Ring & Ball Softening Point | 153 °C | 307 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.6 % | 4.6 % | 50 micron film; ASTM D1003 | ||
| Descriptive Properties | |||||
| MAH Mini | 1600 | ||||