- 密度 [g/cm3]: 0.943
- 拉伸强度 [MPa]: 3.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.943 g/cc | 0.0341 lb/in³ | ASTM D1505 | ||
| Vinyl Acetate Content | 17 - 20 % | 17 - 20 % | Arkema | ||
| Melt Index of Compound | 6.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 84 | 84 | ASTM D2240 | ||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 | ||
| 24.0 MPa | 3480 psi | Film Property, 50 µm thickness; ASTM D882 | |||
| Tensile Strength, Yield | 3.50 MPa | 508 psi | ASTM D638 | ||
| 4.30 MPa | 624 psi | Film Property, 50 µm thickness; ASTM D882 | |||
| Elongation at Break | 600 - 800 % | 600 - 800 % | Film Property, 50 µm thickness; ASTM D882 | ||
| 600 - 900 % | 600 - 900 % | ASTM D638 | |||
| Dart drop Test | 250 g | 0.551 lb | ASTM D1709 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 86.0 °C | 187 °F | DSC | ||
| Vicat Softening Point | 54.0 °C | 129 °F | ASTM D1525 | ||
| Ring & Ball Softening Point | 158 °C | 316 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | 2.5 % | 2.5 % | 50 micron film; ASTM D1003 | ||
| Descriptive Properties | |||||
| MAH Mini | 1600 | ||||