- 熔体流动速率 [g/10min]: 25.0
- 密度 [g/cm3]: 0.948
- 弯曲模量 [MPa]: 0.0150
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 28 % | 28 % | AT Plastics PTM-39 |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 190 °C | 25 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 80 | 80 | ASTM D2240 |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 850 % | 850 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.0150 GPa | 2.18 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Ring & Ball Softening Point | 124 °C | 255 °F | ASTM E28 |