- 密度 [g/cm3]: 0.933
- 拉伸强度 [MPa]: 6.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in³ | ASTM D1505 |
| Vinyl Acetate Content | 9.0 - 11 % | 9.0 - 11 % | |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Index of Compound | 0.50 - 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.50 - 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D638 |
| Tensile Strength, Yield | 6.00 MPa | 870 psi | ASTM D638 |
| Film Elongation at Break, MD | 350 % | 350 % | ASTM D882 |
| Film Elongation at Break, TD | 730 % | 730 % | ASTM D882 |
| Elongation at Break | 720 % | 720 % | ASTM D638 |
| Secant Modulus, MD | 0.0620 GPa | 8.99 ksi | 5%; ASTM D882 |
| Secant Modulus, TD | 0.0610 GPa | 8.85 ksi | 5%; ASTM D882 |
| Film Tensile Strength at Break, MD | 29.0 MPa | 4210 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 99.0 °C | 210 °F | ASTM D3418 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.3 % | 2.3 % | ASTM D1003 |
| Gloss | 82 % | 82 % | 45° - Gardner; ASTM D2457 |
| 130 % | 130 % | @ 60° Gardner; ASTM D2457 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 140 - 155 °C | 284 - 311 °F | Plasticizing Zone |
| 155 - 170 °C | 311 - 338 °F | Mixture Zone | |
| Feed Temperature | 140 - 150 °C | 284 - 302 °F | |
| Adapter Temperature | 170 - 190 °C | 338 - 374 °F | |
| Blow-up Ratio (BUR) | 3.0 | 3.0 | Recommended |