- 熔体流动速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.94
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D792 |
| Moisture Vapor Transmission | 1.42 cc-mm/m²-24hr-atm @Thickness 0.0254 mm | 3.61 cc-mil/100 in²-24hr-atm @Thickness 0.00100 in | g-mm/m²-day; based on film thickness; ASTM E96; ASTM E96 |
| Oxygen Transmission | 264 cc-mm/m²-24hr-atm @Thickness 0.0254 mm | 671 cc-mil/100 in²-24hr-atm @Thickness 0.00100 in | film; ASTM D3985 |
| Melt Flow | 0.70 g/10 min | 0.70 g/10 min | Condition not noted.; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 530 % | 530 % | MD-TD Average; ASTM D882 |
| Film Elongation at Break, TD | 530 % | 530 % | MD-TD Average; ASTM D882 |
| Impact | 31.6 | 31.6 | J/mm Spencer Impact; Average of MD and TD; ASTM D3420 |
| Elmendorf Tear Strength, MD | 4.17 g/micron | 106 g/mil | Average of MD and TD; ASTM D1922 |
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | MD-TD Average; ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 68.0 °C | 154 °F | Freezing Point via DSC/ASTM D3418 |
| 88.0 °C | 190 °F | Freezing Point via DSC/ASTM D3418 | |
| Vicat Softening Point | 67.0 °C | 153 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 28 % | 28 % | ASTM D1003 |
| Gloss | 40 % | 40 % | 20°; ASTM D2457 |