- 密度 [g/cm3]: 0.933
- 弯曲强度 [MPa]: 23.0
- 弯曲模量 [MPa]: 0.0770
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in³ | ASTM D792 | ||
| Vinyl Acetate Content | 12 % | 12 % | TGA | ||
| Melt Index of Compound | 0.30 g/10 min | 0.30 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 96 | 96 | ASTM D2240 | ||
| Hardness, Shore D | 45 | 45 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | Type IV, crosshead speed 2 in/min; ASTM D638 | ||
| 13.0 MPa @Temperature 49.0 °C | 1890 psi @Temperature 120 °F | Type IV, crosshead speed 2 in/min; ASTM D638 | |||
| 38.0 MPa @Temperature -20.0 °C | 5510 psi @Temperature -4.00 °F | Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 | |||
| Elongation at Break | 700 % | 700 % | Type IV, crosshead speed 2 in/min; ASTM D638 | ||
| 500 % @Temperature -20.0 °C | 500 % @Temperature -4.00 °F | Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 | |||
| 800 % @Temperature 49.0 °C | 800 % @Temperature 120 °F | Type IV, crosshead speed 2 in/min; ASTM D638 | |||
| Modulus of Elasticity | 0.0720 GPa | 10.4 ksi | |||
| 0.241 GPa @Temperature -20.0 °C | 35.0 ksi @Temperature -4.00 °F | ||||
| Flexural Modulus | 0.0770 GPa | 11.2 ksi | ASTM D790 | ||
| 0.0340 GPa @Temperature 49.0 °C | 4.93 ksi @Temperature 120 °F | ASTM D790 | |||
| 0.365 GPa @Temperature -20.0 °C | 52.9 ksi @Temperature -4.00 °F | ASTM D790 | |||
| Flexural Stiffness | 72.00 MPa | 10440 psi | |||
| 241.0 MPa | 34950 psi | ||||
| Tensile Impact Strength | 470 kJ/m² | 224 ft-lb/in² | At -20°C; ASTM D1822 | ||
| 590 kJ/m² | 281 ft-lb/in² | At 23°C; ASTM D1822 | |||
| Compression Set | 53 % | 53 % | Method B, 10 days at 25°C; ASTM D395 | ||
| 89 % @Temperature 70.0 °C | 89 % @Temperature 158 °F | Method B, 22 hours; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D762 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 121 - 204 °C | 250 - 399 °F | |||
| Descriptive Properties | |||||
| Cycle time | 0.5-2 minutes | Molding, equipment and part design dependent | |||
| Vinyl Acetate Content | 12 wt.% | ||||