- 熔体流动速率 [g/10min]: 11.0
- 密度 [g/cm3]: 0.927
- 弯曲模量 [MPa]: 0.0931
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in³ | ASTM D1505 |
| Particle Mesh Size | 35 Mesh | 35 Mesh | Irregular shape. ETM = Equistar Test Method; ETM Malvern |
| Melt Flow | 11 g/10 min | 11 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 38 | 38 | ASTM D2240 |
| Tensile Strength at Break | 11.7 MPa | 1700 psi | ASTM D638 |
| Elongation at Break | 675 % | 675 % | ASTM D638 |
| Flexural Modulus | 0.0931 GPa | 13.5 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 96.0 °C | 205 °F | ASTM D3418 |
| Vicat Softening Point | 75.0 °C | 167 °F | ASTM D1525 |
| Brittleness Temperature | -76.0 °C | -105 °F | ASTM D746 |