- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ExxonMobil Method | ||
| Vinyl Acetate Content | 2.0 % | 2.0 % | ExxonMobil Method | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ExxonMobil Method | ||
| Antiblock Level | 3500 ppm | 3500 ppm | |||
| Slip Level | 725 ppm | 725 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 9.10 MPa | 1320 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 9.17 MPa | 1330 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 160 % | 160 % | ASTM D882 | ||
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 6.4 % | 6.4 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 5.5 % | 5.5 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 310 g | 310 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 100 g | 100 g | ASTM D1922 | ||
| Dart drop Test | 140 g | 0.309 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 23.7 MPa | 3440 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 20.7 MPa | 3000 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 172 MPa | 24900 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 208 MPa | 30100 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 107 °C | 224 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 94.0 °C | 201 °F | ExxonMobil Method | ||
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 8.1 % | 8.1 % | ASTM D1003 | ||
| Gloss | 63 % | 63 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||