- 熔体流动速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.933
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in³ | ExxonMobil Method |
| Vinyl Acetate Content | 14.4 % | 14.4 % | ExxonMobil Method |
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | 190°, 2.16 kg; ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 190 % | 190 % | ASTM D882 |
| Film Elongation at Break, TD | 870 % | 870 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 7.68 g/micron | 195 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 2.76 g/micron | 70.0 g/mil | ASTM D1922 |
| Dart Drop | 1.97 g/micron | 50.0 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 33.6 MPa | 4880 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 19.0 MPa | 2750 psi | ASTM D882 |
| 1% Secant Modulus, MD | 110 MPa | 15900 psi | ASTM D882 |
| 1% Secant Modulus, TD | 101 MPa | 14600 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 87.8 °C | 190 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 63.9 °C | 147 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.0 % | 2.0 % | ASTM D1003 |
| Gloss | 81 % | 81 % | 45°; ASTM D2457 |