- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.93
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 6.90 MPa | 1000 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 6.20 MPa | 899 psi | ASTM D882 |
| Film Elongation at Break, MD | 275 % | 275 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Secant Modulus, MD | 0.100 GPa | 14.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.117 GPa | 17.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 150 g | 150 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 100 g | 100 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 4.72 g/micron | 120 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 3.15 g/micron | 80.0 g/mil | ASTM D1922 |
| Dart Drop | 6.30 g/micron | 160 g/mil | F50; ASTM D1709 |
| Dart drop Test | 200 g | 0.441 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.0 MPa | 3050 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 99.0 °C | 210 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 3.0 % | 3.0 % | ASTM D1003 |
| Gloss | 85 % | 85 % | 45°, ASTM D-2457 |