- 熔体流动速率 [g/10min]: 6.5
- 密度 [g/cm3]: 0.925
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 6.5 g/10 min | 6.5 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 5.00 MPa | 725 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 4.90 MPa | 711 psi | ASTM D882 |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 |
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 |
| Secant Modulus, MD | 0.110 GPa | 16.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.117 GPa | 17.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 150 g | 150 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 150 g | 150 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 4.72 g/micron | 120 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.72 g/micron | 120 g/mil | ASTM D1922 |
| Dart Drop | 2.36 g/micron | 60.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 75.0 g | 0.165 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 23.0 MPa | 3340 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 105 °C | 221 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 2.6 % | 2.6 % | ASTM D1003 |
| Gloss | 86 % | 86 % | 45°, ASTM D-2457 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |